Disertación de Maestría
DOI
10.11606/D.85.2018.tde-15062018-105555
Documento
Autor
Nombre completo
Edvan Almeida de Souza Filho
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2017
Director
Tribunal
Pillis, Marina Fuser (Presidente)
Antunes, Renato Altobelli
Araújo, Edval Gonçalves de
Título en portugués
Caracterização de filmes de TiO2, N:TiO2 e TiO2/N:TiO2 obtidos por deposição química de organometálicos em fase vapor
Palabras clave en portugués
dopagem
filmes
MOCVD
multicamada
TiO2
Resumen en portugués
Filmes finos de TiO2 e N:TiO2, e multicamadas TiO2/N:TiO2 foram crescidos sobre substratos de aço AISI 316 e Si(100), por meio da técnica de deposição química de organometálicos em fase vapor (MOCVD). Foram produzidos filmes com diferentes espessuras, nas temperaturas de 400 e 500°C. Os filmes foram caracterizados utilizando-se técnicas de difração de raios X (DRX), espectroscopia de fotoelétrons excitados por raios x (XPS) e microscopia eletrônica de varredura (MEV). A resistência à corrosão foi avaliada por meio de testes de polarização potenciodinâmica em eletrólito 3,5%p NaCl. Filmes não dopados, crescidos a 400°C, apresentaram TiO2 anatase, enquanto que os crescidos a 500°C apresentaram a fase rutilo, além de anatase. Nos filmes dopados com nitrogênio (7,29 e 8,29 at% a 400 e 500°C, respectivamente), em ambas as temperaturas, houve a formação de TiO2 anatase, bem como de fases contendo nitrogênio. Os filmes de TiO2 crescidos a 400°C ofereceram melhor proteção contra a corrosão que os crescidos a 500°C. Filmes crescidos a 500°C apresentaram estrutura colunar, que representa alto nível de porosidade, enquanto que os filmes crescidos a 400°C apresentaram estrutura mais densa. A dopagem não foi eficiente para proteger o substrato contra corrosão, provavelmente devido à formação das fases contendo nitrogênio. Os resultados para os testes com filmes compostos por multicamadas sugerem que aqueles com mais interfaces apresentam melhor resistência à corrosão. O processo de corrosão das amostras se inicia na superfície do filme, que está em contato com o meio agressivo, originando pites, que permitem ao meio corrosivo acessar o substrato metálico. O metal é atacado e dissolvido sob o filme, e resulta na delaminação do filme.
Título en inglés
Characterization of TiO2, N:TiO2 and TiO2/N:TiO2 films obtained by metallorganic chemical vapor deposition
Palabras clave en inglés
doping
films
MOCVD
multilayered
TiO2
Resumen en inglés
TiO2 and N-doped TiO2 (N:TiO2) thin films, and TiO2/N:TiO2 multilayered films were grown on AISI 316 steel substrates, and Si (100) by using metallorganic chemical vapor deposition (MOCVD) technique. The growth of the films was carried out at 400 and 500°C, and films with different thicknesses and structures were obtained. Titanium dioxide films were produced by using only titanium isopropoxide IV as both titanium and oxygen sources. In order to obtain N:TiO2 films, NH3 was also added to the system. The films were characterized by using X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and scanning electron microscopy (SEM) The corrosion resistance was evaluated by potentiodynamic polarization tests in a 3.5wt% NaCl electrolyte. TiO2 undoped films, grown at 400°C, presented anatase, while those grown at 500°C showed the rutile phase, besides anatase. For nitrogendoped films (7.29 and 8.29 at% at 400 and 500°C, respectively), at both temperatures, TiO2 anatase was formed, as well as nitrogen-containing phases. TiO2 films grown at 400°C provided better protection against corrosion than those grown at 500°C. Films grown at 500°C showed a columnar structure, which represents a high level of porosity, while the films grown at 400°C presented a denser structure. Doping was not efficient to protect the substrate against corrosion, probably due to the formation of nitrogen containing phases. The corrosion results for tests with multilayered films suggest that those with more interfaces present better resistance to corrosion. The corrosion of the samples starts at the surface of the films, which is in contact with the aggressive medium, causing pitting in this film, which allows the corrosive medium to reach the metallic substrate. The metal is attacked and dissolved under the film, and results in film delamination.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2018-10-10
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.