Mémoire de Maîtrise
DOI
10.11606/D.85.2009.tde-15102009-153306
Document
Auteur
Nom complet
Karolina Pereira dos Santos Tonello
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2009
Directeur
Jury
Bressiani, Ana Helena de Almeida (Président)
Genova, Luís Antonio
Yoshimura, Humberto Naoyuki
Titre en portugais
Compósitos à base de Al2O3, com adições de NbC e de MgO
Mots-clés en portugais
Alumina
carbeto
compósitos
Resumé en portugais
Avanços tecnológicos geram a necessidade de materiais com propriedades cada vez melhores, de acordo com a sua aplicação final. Compósitos de alumina com adição de partículas de carbeto são uma opção promissora de aplicação estrutural. Neste trabalho foi estudada a influência da diferença de distribuição e tamanho de partículas de duas aluminas comerciais, a adição de 1,5 e 6% em volume de carbeto de nióbio e a adição de 500 ppm de óxido de magnésio, nas propriedades microestruturais e mecânicas de compósitos à base de alumina. Foram preparados corpos de prova por prensagem uniaxial e isostática, sinterizados em forno de resistência de grafite a temperaturas de 1600, 1650, 1700 e 1750°C, por trinta minutos, em atmosfera com pressão positiva de argônio. As amostras obtidas foram avaliadas quanto à densidade, microestrutura e propriedades mecânicas. Também foram realizados ensaios de difusão para verificar a reatividade química entre pares formados por amostras de alumina e ferro fundido cinzento. As características físicas e químicas das aluminas comerciais utilizadas acarretaram diferenças nos materiais finais; os compósitos produzidos com alumina A16 apresentaram densidade maior do que os produzidos com alumina A1000, nas mesmas condições; assim como os valores de dureza também foram maiores. A adição de 6vol% de carbeto de nióbio à matriz de alumina retarda o início da sinterização, enquanto que a adição de 1,5vol% não provoca mudanças sensíveis na cinética de densificação em relação aos materiais sem adição. Os valores de densidade e dureza dos compósitos contendo 1,5vol% de NbC foram superiores nas menores temperaturas de sinterização utilizadas. Os melhores resultados de densificação (>96% Dt) e dureza (>15GPa) foram obtidos para compósitos produzidos com alumina A16 e adição de 1,5% de NbC.
Titre en anglais
Composites based on Al203, with additions of NbC and MgO
Mots-clés en anglais
Alumina
carbeto
compósitos
Resumé en anglais
The worldwide technological advances generate the needs of improved materials with better properties, according to its final purpose. Alumina composites with the addition of carbide particles have become an interesting option for structural applications. This work studies the influence of two commercial aluminas with different particle size and the adding of 1.5 and 6% in volume of niobium carbide and MgO 500 ppm in microstructural and mechanical properties of the composite. Samples were prepared by uniaxial and isostatic pressing and sintering was carried out in a graphite resistance furnace at 1600, 1650, 1700 and 1750°C for thirty minutes in Ar atmosphere. The obtained samples were evaluated sintering behavior, density, microstructure and mechanical properties, diffusion tests were realized to verify chemical reactivity between pairs formed by alumina and gray cast iron samples. The differences between aluminas caused some changes on the composites final properties. The composites produced with A16 alumina presented density about 2% higher than those produced with A1000 alumina. Similarly, the hardness also showed higher values. The carbide niobium added to the matrix of alumina delayed the sintering start, with an increase of about 30% in shrinkage initial states, when 6% of NbC was added. Composite with addition of 1,5% of NbC have higher density and hardness, even at lower sintering temperatures. The adding of niobium carbide to the alumina matrix and higher sintering temperatures provided higher density, hardness and fracture toughness to the composite. The best densification and hardness results of were obtained for composites produced with alumina A16 and when 1.5% of NbC was added.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2009-12-01
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2019. Tous droits réservés.