Mémoire de Maîtrise
DOI
10.11606/D.85.2010.tde-16012013-093254
Document
Auteur
Nom complet
Gonçalo Siqueira
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2010
Directeur
Jury
Rossi, Jesualdo Luiz (Président)
Politano, Rodolfo
Vatavuk, Jan
Titre en portugais
Caracterização microestrutural, mecânica e tratamento térmico da liga AA-6082 obtida pelo processo de conformação por spray
Mots-clés en portugais
conformação por spray
dureza
liga de alumínio AA-6082
solubilização
tratamento térmico
Resumé en portugais
O processo de conformação por spray é interessante devido à capacidade de conjugar, em apenas uma etapa do processo, a vantagem da técnica de solidificação rápida combinada com alta produtividade dos processos de fundição convencional. Este processo permite a obtenção de materiais livre de macrossegregações, livre de porosidades e com microestrutura refinada. A evolução recente das pesquisas está levando ao desenvolvimento de novas ligas e os resultados têm sido interessantes. O processo de solidificação rápida inerente da conformação por spray permite a produção de ligas com composições diferentes das obtidas pela fundição convencional. O objetivo deste trabalho foi o de caracterizar mecanicamente uma liga de alumínio AA-6082 conformada por spray. Os resultados de testes de dureza Vickers são apresentados para seções de um preformado em relação a sua altura (em um arranjo tridimensional). O material foi avaliado na condição como conformado por spray e após tratamento térmico de solubilização a 525 ºC por 1 h, seguido por envelhecimento a 125 ºC por períodos distintos de 1 h, 10 h, 100 h e 500 h. É mostrado que o a liga AA 6082 conformada por spray mostra uma boa estabilidade térmica em relação a variação da dureza durante o envelhecimento.
Titre en anglais
Microstructural characterization, mechanical and heat treatment of the spray formed AA60-82 alloy
Mots-clés en anglais
AA 6082 aluminum alloy
hardness
heat treatment
solution
spray forming
Resumé en anglais
The spray forming technology combines in a single step the advantages of the rapid solidification techniques and high the productivity of the conventional casting processes, allowing obtention of preforms with a refined microstructure, almost without porosity and macrosegregation free. The development and research efforts are leading to interesting alloys and materials production. The rapid solidification processes inherent to the spray forming allow the production of alloys with different compositions from those obtained by conventional ingot processes. The aim of this work was to carry out mechanical properties characterization of a spray formed AA-6082 alloy. The hardness results are presented in different sections related to the height of the spray formed preform (in a three-dimensional arrangement). The material was evaluated in the as sprayed condition and after heat treatment of solution at 525 ºC for 1 h, and aging for 1 h, 10 h, 100 h and 500 h periods. It was shown that the spray formed AA-6082 aluminum alloy is very stable regarding hardness variation during aging.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2013-02-15
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.