Mémoire de Maîtrise
DOI
10.11606/D.85.2011.tde-17062011-103446
Document
Auteur
Nom complet
Tiago Felipe Andrade
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2011
Directeur
Jury
Muccillo, Reginaldo (Président)
Martinelli, José Roberto
Rocha, Renata Ayres
Titre en portugais
Efeito da adição de óxido de zinco e de óxido de boro nas propriedades de zirconato de bário dopado com ítrio
Mots-clés en portugais
condutor protônico
espectroscopia de impedância
óxido de boro
óxido de zinco
zirconato de bário
Resumé en portugais
Compostos condutores protônicos de zirconato de bário dopado com ítrio, BaZr0,8Y0,2O3-δ, preparados por síntese de estado sólido, foram compactados e sinter izados com ZnO e B2O3 como aditivos. Os corpos cerâmicos sinter izados foram analisados por difração de raios X e espectroscopia de impedância. Superfícies polidas e atacadas termicamente foram observadas em microscópio de varredura por sonda. As medidas de densidade mostraram que a maior densificação foi obtida com óxido de zinco nas proporções de 2 e 5 peso%, atingindo aproximadamente 95% da densidade teórica. As medidas de resistividade elétrica evidenciaram a menor resistividade elétrica do composto cerâmico BaZr0,8Y0,2O3-δ, com 5 peso% de ZnO. Os aditivos de sinter ização, óxido de boro e óxido de zinco, foram eficientes para se obter compostos com menores valores de resistividade elétrica que os obtidos em compostos sinter izados sem aditivos.
Titre en anglais
Effect of zinc oxide and boron oxide addition on the properties of yttrium-doped
Mots-clés en anglais
barium zirconate
boron oxide
impedance spectroscopy
protonic conductor
zinc oxide
Resumé en anglais
BaZr0.8Y0.2O3-δ, protonic conductors, prepared by the ceramic route, were pressed and sintered with ZnO and B2O3 sinter ing aids. The sintered pellets were analyzed by X-ra y diffraction and impedance spectroscopy. Polished and thermally etched surfaces of the pellets were observed in a scanning probe microscope. The highest values of apparent densit y, 95%T.D., were obtained with 2 and 5 wt.% ZnO. The lowest value of electr ical resistivit y was obtained in BaZr0.8Y0.2O3-δ, compounds with 5 wt.% ZnO. Boron oxide and zinc oxide sinter ing aids were efficient to improve the apparent densit y as well as the electr ical conductivit y of BaZr0.8Y0.2O3-δ, protonic conductors.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
2011AndradeEfeito.pdf (1.46 Mbytes)
Date de Publication
2011-06-22
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.