Doctoral Thesis
DOI
10.11606/T.85.2017.tde-19012017-092218
Document
Author
Full name
Lia Maria Carlotti Zarpelon
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2016
Supervisor
Committee
Faria Júnior, Rubens Nunes de (President)
Ett, Gerhard
Lima, Nelson Batista de
Marcondes, Paulo Victor Prestes
Seo, Emília Satoshi Miyamaru
Title in Portuguese
Estudo das características eletroquímicas e microestruturais de eletrodos de hidreto metálico à base de LaNi com adições de elementos de liga
Keywords in Portuguese
baterias Ni-MH
eletrodo de hidreto metálico
ligas de armazenamento de hidrogênio
microestrutura
propriedades eletroquímicas
terras raras
Abstract in Portuguese
Neste trabalho avaliou-se a ação positiva da substituição de lantânio por praseodímio e de lantânio por magnésio na performance eletroquímica de eletrodos de ligas de armazenamento de hidrogênio em estado bruto de fusão e com tratamento térmico. O La foi substituído por Mg nas ligas La0,7-xMgxPr0,3Al0,3Mn0,4Co0,5Ni3,8 (x=0,0-0,7) e por Pr nas ligas La0,7-yPryMg0,3Al0,3Mn0,4Co0,5Ni3,8 (y=0,0-0,7). Os parâmetros eletroquímicos analisados foram ativação, capacidade de descarga, retenção da capacidade de descarga, autodescarga e alta taxa de descarga. As ligas apresentaram comportamento passivo em relação à corrosão. As análises por MEV/EDS e por DRX com refinamento por Rietveld revelaram a presença majoritária de fases similares às fases LaNi5, PrNi5, LaMg2Ni9 e PrMg2Ni9 em função das composições das ligas estudadas. Os parâmetros de rede e os volumes da célula unitária das fases diminuíram com a substituição crescente de La por Mg e de La por Pr. As capacidades de descarga máxima decresceram com a substituição crescente de La por Mg e de La por Pr, acompanhando o decréscimo da abundância da fase similar à fase LaNi5 e o aumento da abundância da fase similar à fase LaMg2Ni9. Comparativamente, menores taxas de autodescarga e maior estabilidade cíclica foram observadas para o eletrodo da liga na condição x=0,1, ao passo que o eletrodo da liga na condição y=0,0 apresentou maiores valores de alta taxa de descarga, indicando melhor performance cinética.
Title in English
Study of electrochemical and microstructural characteristics of lani-based metallic hydride electrodes with alloying additions
Keywords in English
alloy structure
electrochemical properties
hydrogen storage alloys
metal hydride electrode
Ni-MH battery
rare earth-based alloys
Abstract in English
In this work, the positive action of the substitution of lanthanum by praseodymium and lanthanum by magnesium in the electrochemical performance of the as-cast and annealed hydrogen storage alloys electrodes had been evaluated. La was replaced by Mg in La0.7-xMgxPr0.3Al0.3Mn0.4Co0.5Ni3.8 (x=0.0-0.7) alloys and by Pr in La0.7-yPryMg0.3Al0.3Mn0.4Co0.5Ni3.8 (y=0.0-0.7) alloys. The electrochemical parameters analyzed were activation, discharge capacity, discharge capacity retention, self-discharge rate and high-rate dischargeability. The alloys showed a passive corrosion behavior. The analyses by SEM/EDS and XRD with Rietveld refinement revealed the majority presence of LaNi5, PrNi5, LaMg2Ni9 and PrMg2Ni9 similar reference phases depending on the compositions of the studied alloys. The lattice parameters and cell volumes of the component phases decreased with increasing substitution of La for Mg and with La for Pr. The maximum discharge capacity decreased with increasing substitution of La for Mg and with La for Pr, following the decrease in the abundance of LaNi5 similar phase and the increase in the abundance of to the LaMg2Ni9 similar phase. Lower self-discharge rates were observed for the alloy electrode when x=0.1, while higher high-rate dischargeability for the alloy electrode when y=0.0 indicated better kinetic performance, comparatively.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2017-03-07
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2020. All rights reserved.