Tesis Doctoral
DOI
10.11606/T.85.2017.tde-19012017-092218
Documento
Autor
Nombre completo
Lia Maria Carlotti Zarpelon
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2016
Director
Tribunal
Faria Júnior, Rubens Nunes de (Presidente)
Ett, Gerhard
Lima, Nelson Batista de
Marcondes, Paulo Victor Prestes
Seo, Emília Satoshi Miyamaru
Título en portugués
Estudo das características eletroquímicas e microestruturais de eletrodos de hidreto metálico à base de LaNi com adições de elementos de liga
Palabras clave en portugués
baterias Ni-MH
eletrodo de hidreto metálico
ligas de armazenamento de hidrogênio
microestrutura
propriedades eletroquímicas
terras raras
Resumen en portugués
Neste trabalho avaliou-se a ação positiva da substituição de lantânio por praseodímio e de lantânio por magnésio na performance eletroquímica de eletrodos de ligas de armazenamento de hidrogênio em estado bruto de fusão e com tratamento térmico. O La foi substituído por Mg nas ligas La0,7-xMgxPr0,3Al0,3Mn0,4Co0,5Ni3,8 (x=0,0-0,7) e por Pr nas ligas La0,7-yPryMg0,3Al0,3Mn0,4Co0,5Ni3,8 (y=0,0-0,7). Os parâmetros eletroquímicos analisados foram ativação, capacidade de descarga, retenção da capacidade de descarga, autodescarga e alta taxa de descarga. As ligas apresentaram comportamento passivo em relação à corrosão. As análises por MEV/EDS e por DRX com refinamento por Rietveld revelaram a presença majoritária de fases similares às fases LaNi5, PrNi5, LaMg2Ni9 e PrMg2Ni9 em função das composições das ligas estudadas. Os parâmetros de rede e os volumes da célula unitária das fases diminuíram com a substituição crescente de La por Mg e de La por Pr. As capacidades de descarga máxima decresceram com a substituição crescente de La por Mg e de La por Pr, acompanhando o decréscimo da abundância da fase similar à fase LaNi5 e o aumento da abundância da fase similar à fase LaMg2Ni9. Comparativamente, menores taxas de autodescarga e maior estabilidade cíclica foram observadas para o eletrodo da liga na condição x=0,1, ao passo que o eletrodo da liga na condição y=0,0 apresentou maiores valores de alta taxa de descarga, indicando melhor performance cinética.
Título en inglés
Study of electrochemical and microstructural characteristics of lani-based metallic hydride electrodes with alloying additions
Palabras clave en inglés
alloy structure
electrochemical properties
hydrogen storage alloys
metal hydride electrode
Ni-MH battery
rare earth-based alloys
Resumen en inglés
In this work, the positive action of the substitution of lanthanum by praseodymium and lanthanum by magnesium in the electrochemical performance of the as-cast and annealed hydrogen storage alloys electrodes had been evaluated. La was replaced by Mg in La0.7-xMgxPr0.3Al0.3Mn0.4Co0.5Ni3.8 (x=0.0-0.7) alloys and by Pr in La0.7-yPryMg0.3Al0.3Mn0.4Co0.5Ni3.8 (y=0.0-0.7) alloys. The electrochemical parameters analyzed were activation, discharge capacity, discharge capacity retention, self-discharge rate and high-rate dischargeability. The alloys showed a passive corrosion behavior. The analyses by SEM/EDS and XRD with Rietveld refinement revealed the majority presence of LaNi5, PrNi5, LaMg2Ni9 and PrMg2Ni9 similar reference phases depending on the compositions of the studied alloys. The lattice parameters and cell volumes of the component phases decreased with increasing substitution of La for Mg and with La for Pr. The maximum discharge capacity decreased with increasing substitution of La for Mg and with La for Pr, following the decrease in the abundance of LaNi5 similar phase and the increase in the abundance of to the LaMg2Ni9 similar phase. Lower self-discharge rates were observed for the alloy electrode when x=0.1, while higher high-rate dischargeability for the alloy electrode when y=0.0 indicated better kinetic performance, comparatively.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2017-03-07
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.