Master's Dissertation
DOI
10.11606/D.85.2011.tde-20122011-165234
Document
Author
Full name
Leandro Cesar Pereira Gomes Safra
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2011
Supervisor
Committee
Rossi, Jesualdo Luiz (President)
Colosio, Marco Antonio
Mucsi, Cristiano Stefano
Title in Portuguese
Obtenção de fios em ligas de cobre para utilização em linhas de transmissão e em eletrodos para contatos elétricos
Keywords in Portuguese
CuCrZr
fio
fusão
liga de cobre
lingote
Abstract in Portuguese
O objetivo do presente trabalho consistiu no desenvolvimento de fios de liga de cobre-cromo-zircônio (CuCrZr) em uma composição estabelecida em Cu-0,7%Cr- 0,1%Zr (em massa). Nas etapas desenvolvidas, foram feitos botões de cobrecromo (CuCr) e cobre-zircônio (CuZr) em um forno a arco elétrico de eletrodo não consumível, sendo esses botões, posteriormente, fundidos junto com cargas de cobre em um cadinho de alumina (Al2O3) inserido no interior de um vaso de aço inoxidável, que serviu como suporte. Após a fusão dos botões e cargas, o banho foi vazado em uma coquilha de cobre, obtendo-se os tarugos da liga de cobre. Dos tarugos em estado bruto de fusão, foram retiradas amostras para ensaios de dureza Vickers. Nesses tarugos foi feito um tratamento térmico de homogeneização a 910 °C por 2 h. Os tarugos foram posteriormente trabalhados mecanicamente a frio por forjamento rotativo seguido de trefilação, para obtenção final dos fios no calibre de 2,174 mm. Os fios passaram por dois tratamentos térmicos de recristalização, um a 510 °C por 1 h e outro de 480 °C por 5 h. Os fios foram caracterizados mecanicamente por ensaios de tração e de dureza e os resultados foram comparados com dados experimentais da literatura.
Title in English
Obtation of cooper-chromium-zirconium alloy wires for use in electrical transmission lines and electrodes for electrical contacts
Keywords in English
copper alloy
CuCrZr
ingot
melting
wire
Abstract in English
The objective of this work is the development of copper alloy wire-chromiumzirconium (CuCrZr) in a chemical composition Cu-0,7% Cr-0,1% Zr (weight). The main steps were, buttons were made of copper-chromium (CuCr) and copperzirconium (CuZr) in an electric arc furnace, these buttons were later melted with copper charge in a alumina crucible, placed inside a stainless steel can which served as a support. After melting buttons and charge, the bath was poured into a copper chill mold obtaining copper alloy billets. From the as cast cooper alloy billets, small samples were cut for Vickers hardness and then, a homogenizing heat treatment at 910 °C for 2 h was performed. The billets were then mechanically cold worked by swaging followed by drawing to obtain the wires with a diameter of 2,174 mm. The wires are mechanically characterized using tensile and hardness testing after recrystallization heat treatment at 510 °C for 1 h and at 480 °C for 5 h and the results were compared with experimental data from literature.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
2011SafraObtencao.pdf (6.48 Mbytes)
Publishing Date
2012-01-30
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2020. All rights reserved.