Tesis Doctoral
DOI
10.11606/T.85.2006.tde-22032012-154040
Documento
Autor
Nombre completo
Omar Fernandes Aly
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2006
Director
Tribunal
Andrade, Arnaldo Homobono Paes de (Presidente)
Agostinho, Silvia Maria Leite
Mattar Neto, Miguel
Monteiro, Waldemar Alfredo
Spinelli, Dirceu
Título en portugués
Modelagem da fratura por corrosão sob tensão nos bocais do mecanismo de acionamento das barras de controle de reator de água pressurizada"
Palabras clave en portugués
corrosão sob tensão
liga 600
mecânica da fratura
modelagem
reatores PWR
Resumen en portugués
Um dos principais mecanismos de falha que causam riscos de fratura a reatores de água pressurizada é a corrosão sob tensão de ligas metálicas em água do circuito primário (CSTAP). É causada por uma combinação das tensões de tração, meio ambiente em temperatura e microestruturas metalúrgicas susceptíveis. Ela pode ocorrer, dentre outros locais, nos bocais do mecanismo de acionamento das barras de controle. Essa fratura pode causar acidentes que comprometem a segurança nuclear através do bloqueio das barras de controle e vazamentos de água do circuito primário reduzindo a confiabilidade e a vida útil do reator. O objetivo desta Tese de Doutorado é o estudo de modelos e uma proposta de modelagem para fraturas por corrosão sob tensão em liga 75Ni15Cr9Fe (liga 600), em água de circuito primário de reator de água pressurizada nesses bocais. São superpostos modelos eletroquímicos e de mecânica da fratura e validados com dados obtidos em experimentos e na literatura. Na parte experimental foram utilizados resultados obtidos pelo CDTN no equipamento recém-instalado de ensaio por taxa de deformação lenta. Na literatura está proposto um diagrama que exprime a condição termodinâmica de ocorrerem diversos modos de CSTAP na liga 600: partiu-se de diagramas de potencial x pH (diagramas de Pourbaix), para a liga 600 imersa em água primária à alta temperatura (3000C a 3500C). Sobre ele, determinaram-se os submodos de corrosão, a partir de dados experimentais. Em seguida acrescentou-se uma dimensão adicional ao diagrama, correlacionando uma variável a que se denominou fração de resistência à corrosão sob tensão. No entanto, é possível acrescentar-se outras variáveis que exprimem a cinética de iniciação e/ou crescimento de trinca, provenientes de outras modelagens de CSTAP. A contribuição original deste trabalho se insere nessa fase: partindo-se de uma condição de ensaio de potencial versus pH, foram iniciadas as modelagens de um modelo empírico-comparativo, um semi-empírico-probabilístico, um de tempo de iniciação e um de taxa de deformação, a partir dos ensaios experimentais e superpostas a essa condição. Esses exprimem respectivamente a susceptibilidade à CSTAP, o tempo de falha, e nos dois últimos o tempo de iniciação de falha por corrosão sob tensão. Os resultados foram comparados com os da literatura e se mostraram coerentes. Através desse trabalho, obteve-se uma metodologia de modelagem a partir de dados experimentais.
Título en inglés
Modeling of primary water stress corrosion cracking at control rod drive mechanism nozzles of Pressurized Water Reactors
Palabras clave en inglés
light water nuclear reactors
models
nickel alloy 600
primary water stress corrosion cracking
slow strain rate test
Resumen en inglés
One of the main failure mechanisms that cause risks to pressurized water reactors is the primary water stress corrosion cracking (PWSCC) occurring in alloys. It can occurs, besides another places, at the control reactor displacement mechanism nozzles. It is caused by the joint effect of tensile stress, temperature, susceptible metallurgical microstructure and environmental conditions of the primary water. These cracks can cause accidents that reduce nuclear safety by blocking the rods displacement and may cause leakage of primary water, reducing the reactors life. In this work it is proposed a study of the existing models and a modeling proposal to primary water stress corrosion cracking in these nozzles in a nickelbased Alloy 600. It is been superposed electrochemical and fracture mechanics models, and validated using experimental and literature data. The experimental data were obtained at CDTN-Brazilian Nuclear Technology Development Center, in a recent installed slow strain rate testing equipment. In the literature it is found a diagram that indicates a thermodynamic condition for the occurrence of some PWSCC submodes in Alloy 600: it was used potential x pH diagrams (Pourbaix diagrams), for Alloy 600 in high temperature primary water (3000C till 3500C). Over it, were located the PWSCC submodes, using experimental data. It was added a third parameter called stress corrosion strength fraction. However, it is possible to superpose to this diagram, other parameters expressing PWSCC initiation or growth kinetics from other models. Here is the proposition of the original contribution of this work: from an original experimental condition of potencial versus pH, it was superposed, an empiric-comparative, a semi-empiric-probabilistic, an initiation time, and a strain rate damage models, to quantify respectively the PWSCC susceptibility, the failure time, and in the two lasts, the initiation time of stress corrosion cracking. It was modeling from our experimental data. The results were compared with the literature and it showed to be coherent. From this work was obtained a modeling methodology from experimental data.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
2006AlyModelagem.pdf (9.56 Mbytes)
Fecha de Publicación
2012-04-04
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.