Master's Dissertation
DOI
10.11606/D.85.2014.tde-22062015-141749
Document
Author
Full name
Pamela Karina dos Santos Bomfim
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2014
Supervisor
Committee
Neves, Maurício David Martins das (President)
Barbosa, Lusinete Pereira
Rodrigues, Daniel
Title in Portuguese
Desenvolvimento de implantes dentários por técnicas de metalurgia do pó
Keywords in Portuguese
biocompatibilidade
metalurgia do pó
porosidade
Abstract in Portuguese
O interesse crescente no desenvolvimento de biomateriais com superfície porosa para aplicações dentárias decorre do suporte propicio ao crescimento do tecido ósseo, aumentando a adesão entre o tecido e material, favorecendo a osteointegração. O titânio pode ser considerado um ótimo material para implantes dentários, pela sua excelente biocompatibilidade, elevada resistência à corrosão e combinação de alta resistência com baixa densidade. Contudo, a alta reatividade do metal no estado líquido acaba dificultando a fabricação de implantes por fundição, sendo a metalurgia do pó composta por técnicas que permitem a obtenção de peças em temperaturas menores de processamento (estado sólido) e com módulo elástico próximo ao do tecido ósseo. O objetivo deste trabalho foi avaliar amostras porosas obtidas pela Metalurgia do Pó (MP) convencional. Inicialmente o pó de titânio comercialmente puro (Ti-cp) obtido pelo processo de hidretação-dehidretação (HDH), foi compactado em matriz uniaxial e sinterizado a vácuo em duas temperaturas,1100 e 1150°C/1h. As amostras sinterizadas foram caracterizadas quanto à densidade, porosidade, microestrutura ( microscopia óptica - MO e microscopia eletrônica de varredura - MEV), fases cristalinas (difração de raios - X - DRX), propriedades mecânicas (microdureza e ensaio de flexão em três pontos), comportamento eletroquímico (potencial de circuito aberto, espectroscopia de impedância eletroquímica e polarização anódica) e o ensaio de imersão foram empregados nas amostras obtidas por (MP) e no titânio fundido. Os resultados indicaram morfologia angular, distribuição granulométrica com média de 45 μm, além de densidade aparente e escoabilidade baixas. Foram obtidas amostras com porosidade de aproximadamente 33% e poros interligados dentro de uma faixa de tamanho de 110 140 μm. As análises por MEV e DRX das amostras sinterizadas indicaram a presença de fase α e poros. As amostras sinterizadas a 1150°C revelaram melhor comportamento mecânico em relação as amsotras sinterizadas a 1100°C. As análises eletroquímicas indicaram a elevada resistência a corrosão do titânio fundido, seguida pela amostra sinterizada 1100°C e finalmente das sinterizadas a 1150°C, quando imersas em solução da saliva artificial. O EDS foi executado para verificar a deposição de elementos na superfície. Testes de citotoxicidade demonstraram que o pó e as amostras sinterizadas não apresentaram qualquer efeito tóxico em culturas celulares. As amostras sinterizadas à 1100°C possuiam grau de porosidade e tamanho de poros que favoreceram o crescimento do tecido ósseo, além do módulo de elasticidade próximo ao tecido ósseo e foram mais resistentes a corrosão na solução simuladora.
Title in English
Development of the dental implants by powder metallurgy techniques
Keywords in English
biocompatibility
porosity
powder metallurgy
Abstract in English
The development of materials with a porous surface has been widely studied in the field of biomaterials, because the porous structure allows bone tissue growth, increasing the bonding since the tissue and the material, favoring osteointegration. Given the excellent biocompatibility, high corrosion resistance and combination of high strength with low density, titanium is one of the most suitable materials for dental implants. However, the high reactivity in liquid state ends up hindering their fusion. The technique of powder metallurgy (PM) is an alternative for cost reduction, allowing to obtain superior samples at lower temperatures, closer to the bone tissue in terms of elastic modulus. The objective of this study was to evaluate porous samples obtained by conventional PM. Initially the powder of commercially pure titanium (cp-Ti) was obtained by hydridedehydride (HDH) process, followed by uniaxial pressing and vacuum sintering at 1100 and 1150 °C/1h. The sintered samples were characterized - density, porosity, microstructure (SEM), crystalline phases (XRD), mechanical properties (microhardness and three point bending test), electrochemical behavior (open circuit potential, anodic polarization and electrochemical spectroscopy impedance and immersion essay) applied in porous samples and cast titanim The results indicated angular particle morphology, 45 μm average particle size distribution, low apparent density and flowability. The different processing temperatures enabled to obtain samples with approximately 33 % interconnected porosity and average pore size in 110-140μm range. SEM and XRD analysis of the sintered samples revealed the presence of α phase and pores. Samples sintered at 1150°C showed superior mechanical behavior. Electrochemical analysis (in artificial saliva solution) indicated higher corrosion resistance of cast titanium compared to porous samples . Cytotoxicity tests proved that the powder and sintered samples has no toxic effects on cell cultures. Samples sintered at 1100 °C excels in bone growth stimulation, elasticity modulus and corrosion resistance, due to superior porosity and pore size range properties, creating a material analogous to the bone.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2015-07-17
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2021. All rights reserved.