Master's Dissertation
DOI
10.11606/D.85.2016.tde-22082016-143920
Document
Author
Full name
Edvaldo Roberto de Souza
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2012
Supervisor
Committee
Neves, Maurício David Martins das (President)
Berretta, José Roberto
Delijaicov, Sergio
Title in Portuguese
Caracterizações microestruturais e avaliações das propriedades mecânicas das juntas em aço inoxidável AISI 301 L soldadas por MIG e submetidas ao reparo pelo processo TIG
Keywords in Portuguese
aço inoxidável
refusão
reparo
retrabalho
TIG
Abstract in Portuguese
A soldagem tem grande importância no setor metroferroviário, pois é empregada na fabricação de componentes estruturais e no acabamento de vagões de passageiros, que em sua maior parte são de aço inoxidável. As juntas soldadas podem apresentar descontinuidades que são interrupções que afetam as propriedades mecânicas e metalúrgicas da junta soldada. A presença destas descontinuidades, dependendo do seu tamanho, natureza ou efeito combinado, pode ocasionar a reprovação da junta soldada, quer pela redução de propriedades mecânicas ou pela não aceitação, segundo critérios estabelecidos em normas. Uma estrutura que tenha uma solda reprovada durante sua qualificação ou inspeção, pela presença de descontinuidades pode ser recuperada, por meio de um retrabalho a ser realizado nesta junta. A refusão do cordão de solda por meio do processo TIG (Tungsten Inert Gas), sem a utilização do material de adição, é uma técnica de retrabalho que pode ser empregada, em especial pela viabilidade técnica e econômica do processo. Neste estudo analisou-se a influência que o processo de reparo por soldagem TIG exerceu no comportamento mecânico e microestrutural das juntas soldadas pelo processo MIG, por meio de: ensaios mecânicos (tração, fadiga e microdureza Vickers), ensaios não destrutivos (inspeção visual e líquidos penetrantes) e caracterização microestrutural do cordão de solda. Resultados das amostras de ensaio de tração e fadiga indicaram que o reparo dos cordões de solda não alterou o comportamento mecânico das juntas. As juntas submetidas ao reparo nas quais foram retirados os reforços dos cordões apresentaram modificações nas propriedades mecânicas, mas também apresentaram resultados satisfatórios.
Title in English
Microstructural characterization and evaluation of mechanical properties of joints in steel AISI 301 L welded by MIG and submitted to repair by TIG process
Keywords in English
remelting
repair
rework
stainless steel
TIG
Abstract in English
The welding has great importance in manufacture of subway cars because it is used in the manufacture of structural components and finishing in passenger cars which are mostly stainless steel. Joints may show the presence of discontinuities. The discontinuities are interruptions that affect the mechanical and metallurgical properties of the weld. The presence of these discontinuities, depending on their size, nature or the combined effect may lead to failure of the weld either by reduction of mechanical properties or non-acceptance criteria established in standards. A structure that has a weld failed during its qualification or inspection by the presence of discontinuities can be retrieved through a rework to be done in this joint. The remelting of the weld using the TIG process without the use of additional material, rework is a technique that can be employed in particular the technical and economic feasibility of the process. This study analyzes the influence that the process of TIG welding rework has on mechanical behavior and microstructure of welded joints by means of: mechanical tests (tensile and Vickers hardness), non-destructive testing (visual inspection and liquid penetrant) and characterization microstructure of the weld. Results of tensile test specimens and fatigue indicated that the repair of the weld beads did not change the mechanical behavior of joints. The joints subjected to repair in which they were removed the ribs of the beads showed changes in the mechanical properties, but also had satisfactory results.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2016-08-25
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2020. All rights reserved.