Mémoire de Maîtrise
DOI
https://doi.org/10.11606/D.85.2016.tde-22082016-155447
Document
Auteur
Nom complet
Marcos Yovanovich
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2016
Directeur
Jury
Oliveira Neto, Almir (Président)
Ayoub, Jamil Mahmoud Said
Farias, Luciana Aparecida
Titre en portugais
Oxidação eletroquímica do ácido fórmico em eletrólito ácido e básico utilizando eletrocatalisadores PtBi/C e PdBi/C preparados pelo método de redução via borohidreto de sódio adição rápida
Mots-clés en portugais
ácido fórmico
borohidreto de sódio
PdBi/C
PtBi/C
Resumé en portugais
PtBi/C e PdBi/C foram preparados em diferentes razões atômicas (100:0, 90:10, 80:20, 70:30, 60:40 e 50:50) pelo método de redução via borohidreto de sódio (com adição total da solução de borohidreto em uma única etapa) utilizando H2PtCl6.6H2O, Pd(NO3)2, (BiNO3)3.5H2O como fonte de metais, Vulcan® (XC72-Cabot) como suporte de carbono e com uma carga metálica correspondente a 20% em massa. Os eletrocatalisadores obtidos foram caracterizados por difração de raios-X (DRX), microscopia eletrônica de transmissão (MET) e voltametria cíclica (VC). A atividade dos diferentes materiais preparados para a oxidação eletroquímica do ácido fórmico foi realizada em eletrólito ácido e alcalino utilizando-se as técnicas de voltametria cíclica, e cronoamperometria. Para estes estudos foi utilizado a técnica do eletrodo de camada fina porosa. A caracterização eletroquímica permitiu comparar o desempenho eletroquímico da platina e paládio, além de avaliar o benefício da presença do bismuto nas razões atômicas propostas. Os difratogramas de raio-X (DRX) confirmaram para todos os compostos de PtBi/C e PdBi/C a formação da estrutura cúbica de face centrada (cfc) característicos da rede cristalina da platina e do Paládio respectivamente. Outros picos encontrados foram associados a presença de fases de óxido de bismuto em ambos os compostos, PtBi/C e PdBi/C. A microscopia eletrônica de transmissão (MET) indicou que a presença de maiores teores de bismuto não acarretaram em aumento do tamanho médio da partícula. Os resultados eletroquímicos em meio alcalino indicaram que ainda é necessário uma otimização da concentração de ácido fórmico para que possamos observar melhores resultados quanto à adição de bismuto na platina ou paládio, no entanto os estudos em meio ácido mostraram o efeito benéfico da adição de bismuto tanto para platina quanto para o paládio.
Titre en anglais
Electrochemical oxidation of formic acid in acid and alkaline electrolyte using electrocatalysts PtBi/C and PdBi/C prepared via sodium borohydride reduction method in a fast manner
Mots-clés en anglais
formic acid
PdBi/C
PtBi/C
sodium borohydride
Resumé en anglais
PtBi/C and PdBi/C were prepared with different atomic ratios (100:0, 90:10, 80:20, 70:30, 60:40 and 50:50) by sodium borohydride reduction method (with total addition of the borohydride solution in just one step) using H2PtCl6.6H2O, Pd(NO3)2, (BiNO3)3.5H2O as source of metals, Vulcan® (XC72-Cabot) as carbon support and a metallic charge correspondent to 20% mass. The obtained electrocatalysts were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM) and cyclic voltammetry (CV). The activity of the different materials used for the formic acid electrochemical oxidation was performed in acid and alkaline electrolyte through cyclic voltammetry and chronoamperometry, using the porous thin-film electrode technique. The electrochemical characterization allowed for the comparison between the platinum and palladium electrochemical performance, as well as the evaluation of the benefit of having bismuth in the proposed atomic ratios. The X-ray diffraction (XRD) diffractograms confirmed, for every PtBi/C and PdBi/C compounds, the formation of the face-centered cubic structure (fcc) distinctive to platinum and palladiums crystalline net, respectively. Other peaks were found associated to the presence of bismuth oxide phases in both compounds, PtBi/C and PdBi/C. The transmission electron microscopy (TEM) indicated that a higher bismuth presence did not result in a larger particle size. The electrochemical results in alkaline medium indicated that an optimization on formic acid concentration is still necessary so that better results concerning bismuth addition to platinum or palladium could be observed, although the studies done in acid medium presented the beneficial effect of bismuth addition to both platinum and palladium.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2016-08-25
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2024. Tous droits réservés.