Disertación de Maestría
DOI
https://doi.org/10.11606/D.85.2009.tde-22092011-101543
Documento
Autor
Nombre completo
Leonardo Calicchio
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2009
Director
Tribunal
Pillis, Marina Fuser (Presidente)
Ambrozio Filho, Francisco
Vatavuk, Jan
Título en portugués
Efeito do 'shot peening' sobre a nitretação de peças de ferro produzidas por metalurgia do pó
Palabras clave en portugués
metalurgia do pó
nitretação
shot peening
Resumen en portugués
Atualmente, quando se tem a necessidade de nitretar peças produzidas pela metalurgia do pó, usa-se a nitretação a plasma. Apesar de ser um processo de alto custo, com diversas dificuldades operacionais e de ajuste de processo, a nitretação a plasma é o único processo viável para nitretar esses materiais por ter uma ação apenas superficial, não apresentando ação nitretante no interior dos poros. Nos processos de nitretação a gás e banho de sais, o meio nitretante penetra na porosidade (interconectada) dos materiais sinterizados, havendo assim a formação de camada branca em uma grande profundidade da peça (ou mesmo na peça toda), gerando problemas de deformação e fragilização do componente. Este trabalho teve por objetivo a aplicação do processo shot peening em peças sinterizadas com a finalidade de fechar a porosidade superficial das peças e estudar seu comportamento sob o processo de nitretação a gás. O estudo verifica que o material sinterizado submetido à nitretação gasosa permitiu a entrada do meio nitretante pelos poros abertos e interconectados promovendo a formação de camada branca no interior dos poros de praticamente todo o volume da peça. Essa camada branca no interior do material fragiliza o componente e inviabiliza sua utilização como componente em praticamente qualquer aplicação industrial. As peças sinterizadas jateadas com granalhas de aço antes da nitretação também permitiram o acesso do meio nitretante no interior do componente, porém, sem potencial suficiente para a formação de camada branca. As amostras jateadas apresentaram apenas agulhas de nitretos formados durante a nitretação.
Título en inglés
The effect of shot peening on the gas nitriding of iron components produced by powder metallurgy
Palabras clave en inglés
iron
iron nitrides
nitridation
nitrogen compounds
powder metallurgy
shot peening
surface treatments
Resumen en inglés
Plasma nitriding is the process used to nitriding components produced by powder metallurgy. Although its high coast and operational difficulties, this is the best process for this kind of materials because the nitring occurs only in the surface. In gas and liquid nitriding processes the nitriding atmosphere goes through interconnected porous and the white layer forms not only on the surface but around internal porous resulting in embrittlement and deformation of the component. The aim of this work was evaluate the gas nitriding behavior of iron samples as received and previously submitted to shot peening process in order to close superficial porosities in a gas nitriding process. The results have shown that during gas nitriding the samples as received, did not present white layer at the surface but around the porous in the bulk of the sample. This fact suggested that the gaseous atmosphere goes through interconnected porous. This white layer causes the embrittlement of the component and its use in industrial application is not recommended. Otherwise, samples previously submitted to shot peening process before nitriding showed an external white layer but also permitted the access of nitriding atmosphere to the bulk of the sample, but in this case the nitriding potential was not sufficient to form white layer around internal porous.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2012-07-23
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.