Doctoral Thesis
DOI
https://doi.org/10.11606/T.85.2017.tde-23102017-160802
Document
Author
Full name
Rodolfo Molina Antoniassi
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2017
Supervisor
Committee
Spinacé, Estevam Vitorio (President)
Assumpção, Mônica Helena Marcon Teixeira
Camargo, Pedro Henrique Cury
Lazar, Dolores Ribeiro Ricci
Otubo, Larissa
Title in Portuguese
Preparação de nanopartículas de platina com diferentes morfologias nos materiais Pt/C e PtSnO2/C para aplicação como ânodo em células a combústível de etanol direto
Keywords in Portuguese
DEFC
eletro-oxidação de etanol metanol e CO2
nanopartículas cúbicas de Pt
Pt(100)
PtSnO2/C
Abstract in Portuguese
Neste trabalho foi estudado o efeito da adição de íons haletos (Cl-, Br- e I-) sobre a morfologia das nanopartículas de Pt na produção de catalisadores de Pt/C e PtSnO2/C. Foi desenvolvida uma metodologia de síntese simples capaz de produzir nanopartículas de Pt predominantemente cúbicas com orientação preferencial Pt(100), diretamente suportadas em carbono sem o uso de agentes estabilizantes. Brometo de potássio foi utilizado como agente direcionador de superfície para obtenção do material preferencialmente orientado. O controle de adição do precursor de Pt e de KBr foi crucial para obter nanocubos de Pt de 8 nm bem dispersos sobre o suporte. Na preparação dos catalisadores de PtSnO2/C, o processo de adição do SnCl2 também foi decisivo na obtenção das nanopartículas de Pt com tamanho e morfologia de interesse. Nanocubos de Pt coexistindo com SnO2 disperso foram exclusivamente obtidos ao adicionar o SnCl2 na etapa final da síntese, quando as nanopartículas cúbicas de Pt já estavam formadas. Enriquecidos de domínios Pt(100), os materiais em forma cúbica de Pt/C e PtSnO2/C se mostraram menos afetados pelo acúmulo dos intermediários indesejados provenientes da reação de eletro-oxidação de etanol e foram mais tolerantes ao envenenamento por monóxido de carbono. Resultados similares foram observados para a oxidação de CO e metanol, utilizados como apoio para compreensão da eletro-oxidação de etanol. O efeito morfológico destes materiais no desempenho elétrico em célula a combustível de etanol direto foi avaliado. Pt/C e PtSnO2/C contendo nanopartículas de Pt com orientação preferencial Pt(100) forneceram maiores valores de densidade de potência e de seletividade para CO2 comparados aos catalisadores de Pt/C e PtSnO2/C com nanopartículas de Pt sem orientação preferencial.
Title in English
Preparation of platinum nanoparticles with different morphologies in Pt/C and PtSnO2/C materials for anode direct ethanol fuel cell application
Keywords in English
DEFC
ethanol methanol and CO2 electro-oxidation
Pt cubic nanoparticles
Pt(100)
PtSnO2/C
Abstract in English
The effect of the addition of halide ions (Cl-, Br- and I-) on the shape of Pt nanoparticles of Pt/C and PtSnO2/C catalysts was studied in this work. It was developed a simple methodology synthesis capable of producing Pt nanoparticles predominantly cubic with Pt(100) preferential orientation, directly supported on carbon without the use of stabilizing agents. Potassium bromide was used as a surface directing agent to obtain the preferentially oriented material. The control in addition of the Pt precursor and KBr was crucial to obtain well dispersed 8 nm Pt nanocubes on the support. For the preparation of PtSnO2/C catalysts, the addition process of SnCl2 was also decisive to obtain the Pt nanoparticles with desirable size and morphology. Pt nanocubes coexisting with disperse SnO2 were exclusively obtained by adding SnCl2 in the final step of the synthesis, when the cubic Pt nanoparticles were already formed. Enriched with Pt (100) domains, the Pt/C and PtSnO2/C cubic materials were less affected by the undesirable intermediates accumulation from the ethanol electro-oxidation reaction and were more tolerant to the poisoning of monoxide carbon. Similar results were observed for methanol and CO electro-oxidation reactions, which were employed to understand ethanol electro-oxidation. The morphological effect of these materials on electrical performance in direct ethanol fuel cell was evaluated. Pt/C and PtSnO2/C containing Pt(100) nanoparticles provided higher power density and CO2 selectivity values compared to Pt/C and PtSnO2/C catalysts with Pt nanoparticles without ant preferential orientation.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2017-11-06
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2024. All rights reserved.