Disertación de Maestría
DOI
10.11606/D.85.2017.tde-26102017-141238
Documento
Autor
Nombre completo
Aline de Fátima Santos Bugarin
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2017
Director
Tribunal
Costa, Isolda (Presidente)
Melo, Hercilio Gomes de
Terada, Maysa
Título en portugués
Estudo da resistência à corrosão das ligas de alumínio 2024-T3 e 7475-T651 soldadas por fricção e mistura (FSW)
Palabras clave en portugués
AA2024 e AA7475
resistência à corrosão
soldagem de ligas de alumínio dissimilares
soldagem por fricção e mistura (FSW)
Resumen en portugués
O processo de soldagem por fricção e mistura (FSW) tem despertado grande interesse nos últimos anos e tornou-se uma alternativa para unir materiais de baixa soldabilidade, como as ligas de alumínio das séries 2XXX e 7XXX, as quais são empregadas na estrutura das aeronaves, por possuírem elevada relação resistência/peso. O processo FSW, todavia, causa mudanças microestruturais nos materiais soldados, particularmente na zona misturada (ZM) e nas zonas termicamente (ZTA) ou termomecanicamente (ZTMA) afetadas. Estas mudanças geralmente interferem no desempenho frente à corrosão das ligas soldadas. No presente estudo, a resistência à corrosão das ligas de alumínio 2024-T3 e 7475-T761, unidas pelo processo FSW foi investigada em solução 10 mM de NaCl. Ensaios de visualização em gel ágar-ágar e de imersão associados a técnicas microscópicas foram realizados para investigar o efeito do acoplamento galvânico na corrosão das diferentes regiões da junta soldada. Os resultados do ensaio de visualização em gel mostraram que, quando acopladas, a liga 2024 atua como cátodo e a 7475 como ânodo. Os ensaios de imersão revelaram acoplamento galvânico entre as ligas na zona misturada (ZM). A região mais afetada pela corrosão foi a ZTMA da liga 7475, com corrosão intergranular desde as primeiras horas de imersão. A influência do processo de soldagem na resistência à corrosão das duas ligas de alumínio foi investigada por ensaios eletroquímicos. Os ensaios eletroquímicos adotados foram medidas de potencial de circuito aberto (PCA) em função do tempo de exposição ao meio corrosivo, espectroscopia de impedância eletroquímica (EIE) e curvas de polarização potenciodinâmica. Os ensaios de polarização mostraram elevada atividade eletroquímica na zona de mistura indicada pelos altos valores de densidade de corrente em comparação com as demais zonas testadas. Os resultados de EIE globais mostraram que nas primeiras horas de exposição ao eletrólito o processo de corrosão foi predominantemente controlado pela liga 7475; todavia, com o tempo de exposição ao eletrólito, a corrosão passou a ser controlada pela liga 2024.
Título en inglés
Study of the corrosion resistance of aluminium alloys 2024-T3 and 7475-T651 welded by friction stir welding (FSW)
Palabras clave en inglés
AA2024 and AA7475
corrosion resistence
friction stir welding (FSW)
welding of aluminum dissimilar alloys
Resumen en inglés
Friction stir welding (FSW) has roused great interest in recent years and it is now an alternative for joining materials of low weldability, such as the aluminum alloys of the 2XXX and 7XXX series, used in the aircrafts structure due to their high strength /weight ratio. However, FSW causes material microstructural changes, mainly in the stir zone (SZ), the heat affected zone (HAZ) or thermomechanically (TMAZ) affected zones of the materials welded. These generally interfere with the corrosive performance of the welded joint. In the present study, the corrosion resistance of the 2024-T3 and 7475-T761aluminum alloys, joined by FSW was investigated in 10 mM NaCl electrolyte. Agar-agar gel and immersion tests associated with microscopic techniques were performed to investigate the effect of galvanic coupling between the welded materials. Results from this test showed that, when galvanically coupled, the 2024 alloy acts as cathode and the 7475 as anode. Immersion tests revealed galvanic coupling between the alloys in the SZ. The zone most susceptible to corrosion was the TMAZ of the 7475. Intergranular corrosion was observed in this zone since the first hours of immersion. The influence of the welding process on the corrosion resistance of the alloys was also evaluated by electrochemical tests. The electrochemical tests adopted were open circuit potential measurements (OCP) as a function of time of exposure to the electrolyte, electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization curves. The polarization tests showed high electrochemical activity in the stir zone indicated by the high current densities measured comparatively to the other tested zones. The global EIS results indicated that in the first few hours of exposure to the electrolyte the corrosion process was predominantly controlled by the 7475 alloy; however, with time of exposure to the electrolyte, the corrosion was controlled by alloy 2024.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
2017BugarinEstudo.pdf (5.87 Mbytes)
Fecha de Publicación
2017-11-06
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.