Tesis Doctoral
DOI
https://doi.org/10.11606/T.85.2017.tde-27042017-154740
Documento
Autor
Nombre completo
Gisele Fabiane Costa Almeida
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2017
Director
Tribunal
Couto, Antonio Augusto (Presidente)
Martins, Gislene Valdete
Massi, Marcos
Monteiro, Waldemar Alfredo
Silva Sobrinho, Argemiro Soares da
Título en portugués
Estudo do comportamento mecânico em temperaturas elevadas da liga Ti-6Al-4V após tratamento superficial de nitretação por plasma
Palabras clave en portugués
fluência
nitretação por plasma
Ti-6Al-4V
Resumen en portugués
A liga Ti-6Al-4V é uma das ligas de titânio mais suas aplicações estruturais em temperaturas elevadas são limitadas devido a sua afinidade pelo oxigênio. Um tratamento superficial que melhore a resistência à oxidação desta liga permitindo a substituição de peças que atualmente são produzidas com superligas de Ni por este material, poderia reduzir significativamente o peso destes componentes. O objetivo deste trabalho é melhorar a resistência à fluência desta liga utilizando nitretação por plasma. Para homogeneizar a microestrutura do material, foi realizado um tratamento térmico a 1050ºC por 30 minutos para obtenção da microestrutura de Widmanstätten que foi a que apresentou melhor resistência à fluência no material sem tratamento. A nitretação foi realizada variando parâmetros de processo como tempo, temperatura e mistura de gases na atmosfera. A partir dos resultados obtidos, a mistura de gás de Ar:N2:H2 (0,49:0,49:0,03) a 700°C por 4 horas foi a condição escolhida. A caracterização da camada nitretada foi realizada por técnicas de microscopia ótica e eletrônica de varredura, além de difração de raios X. As fases da amostra nitretada detectadas por DRX foram o ε-Ti2N e δ-TiN, além das fases α e β da matriz. A espessura da camada nitretada foi de cerca de 1 μm. Os ensaios de tração a quente foram realizados em temperaturas entre 500°C e 700°C no material com e sem nitretação e mostraram um aumento na resistência da liga nitretada de até 29% nos limites de escoamento e resistência. Os ensaios de fluência foram realizados variando a temperatura também entre 500 e 700ºC e tensão aplicada entre 125 e 319 MPa. O resultado foi um aumento na resistência à fluência do material nitretado. Isto foi evidenciado pela diminuição da taxa de fluência secundária e também pelo aumento do tempo de ruptura do material.
Título en inglés
High temperature mechanical behavior of the TI-6AL-4V alloy after plasma nitriding
Palabras clave en inglés
creep
plasma nitriding
Ti-6Al-4V
Resumen en inglés
The Ti-6Al-4V alloy is one of the most widely used titanium alloys, but its structural applications at elevated temperatures are limited because of the titanium high affinity for oxygen. A surface treatment that improves the oxidation resistance of this alloy allowing the replacement of parts that are currently produced with Ni-based super alloys by this material could significantly reduce the weight of these components. The aim of this work is to improve the creep resistance of the Ti-6Al-4V alloy using plasma nitriding. In order to homogenize the material microstructure, it was performed a heat treatment at 1050ºC for 30 minutes to obtain the Widmanstätten microstructure, which was the that presented better resistance to creep in the no nitrided material. The nitriding was performed by varying parameters as time, temperature and gas mixture in the atmosphere during the process. The chosen condition was a gas mixture of Ar: N2: H2 (0.49: 0.49: 0.03) at 700°C for 4 hours. The compound layer characterization was performed by optical and scanning electron microscopy techniques and X-ray diffraction. The nitrided samples phases detected by XRD were ε-Ti2N, δ-TiN and the α-Ti and β-Ti matrix phases. The layer thickness of this sample was about 1 μm. The hot tensile tests were performed in a temperature range from 500°C to 700°C in nitrided and no nitrided materials and show an increase in the strength of the nitrided alloy up 29% in yield and ultimate strength. The creep tests were also performed in a temperature between 500 and 700ºC and stress range from 125 to 319 MPa. The results showed an increase in nitrided sample creep resistance. This was evidenced by both the decrease in secondary creep rate and an increase in final creep time.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
2017AlmeidaEstudo.pdf (4.70 Mbytes)
Fecha de Publicación
2017-05-08
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.