• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Disertación de Maestría
DOI
10.11606/D.85.2013.tde-28082013-090145
Documento
Autor
Nombre completo
José Carlos de Castro
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2013
Director
Tribunal
Oliveira Neto, Almir (Presidente)
Farias, Luciana Aparecida
Silva, Dionisio Furtunato da
Título en portugués
Desempenho de eletrocatalisadores PtSnRh suportados em carbono-Sb2O5.SnO2 para a oxidação eletroquímica do etanol, preparados pelo método de redução por álcool
Palabras clave en portugués
células a combustível de etanol direto
efeito eletrônico
método de redução por álcool
oxidação eletroquímica do etanol
PtSnRh/C-Sb2O5.SnO2
Resumen en portugués
Os eletrocatalisadores PtSnRh suportados em carbono-Sb2O5.SnO2, com 20% de massa de metal, foram preparados pelo método de redução por álcool, utilizando H2PtCl6.6H2O (Aldrich), RhCl3.xH2O (Aldrich) e SnCl2.2H2O (Aldrich), como fontes de metais; Sb2O5.SnO2 (ATO) e carbono Vulcan XC72, como suporte; e etileno glicol como agente redutor. Os eletrocatalisadores obtidos foram caracterizados fisicamente por difração de raios-X (DRX) e microscopia eletrônica de transmissão (MET). Por meio dos difratogramas observou-se que os eletrocatalisadores PtSnRh/C-ATO possuem estrutura CFC para a Pt e ligas de Pt, além de vários picos associados ao SnO2 e ATO. Os tamanhos médios dos cristalitos ficaram entre 2 e 4 nm. Por meio das micrografias verificou-se uma boa distribuição das nanopartículas sobre o suporte. Os tamanhos médios das partículas ficaram entre 2 e 3 nm, com boa concordância para os tamanhos médios dos cristalitos. Os desempenhos dos eletrocatalisadores foram analisados por meio de técnicas eletroquímicas e em condições reais de operação utilizando uma célula a combustível unitária alimentada diretamente por etanol. Na cronoamperometria, a temperatura de 50ºC, os eletrocatalisadores com proporção de 85%C+15%ATO para o suporte, apresentaram a melhor atividade, e as proporções atômicas que obtiveram os melhores resultados foram PtSnRh(70:25:05) e (90:05:05). Nos experimentos em célula, o eletrocatalisador PtSnRh(70:25:05)/85C+15ATO apresentou o melhor desempenho.
Título en inglés
Performance PtSnRh electrocatalysts supported on carbon-Sb2O5.SbO2 for the electro-oxidation of ethanol, prepared by an alcohol-reduction process
Palabras clave en inglés
alcohol reduction process
direct ethanol fuel cells
electronic effect
ethanol electro-oxidation
PtSnRh/C-Sb2O5.SnO2
Resumen en inglés
PtSnRh electrocatalysts supported on carbon-Sb2O5.SnO2, with metal loading of 20 wt%, were prepared by an alcohol-reduction process, using H2PtCl6.6H2O (Aldrich), RhCl3.xH2O (Aldrich) and SnCl2.2H2O (Aldrich), as source of metals; Sb2O5.SnO2 (ATO) and carbon Vulcan XC72, as support; and ethylene glycol as reducing agent. The electrocatalysts obtained were characterized physically by X-ray diffraction (XRD) and transmission electron microscopy (TEM). The diffractograms showed which PtSnRh/C-ATO electrocatalysts had FCC structure of Pt and Pt alloys, besides several peaks associated with SnO2 and ATO. The average sizes of crystallites were between 2 and 4 nm. TEM micrographs showed a good distribution of the nanoparticles on the support. The average sizes of particles were between 2 and 3 nm, with good agreement for the average size of the crystallites. The performances of the electrocatalysts were analyzed by electrochemical techniques and in real conditions of operation using single direct ethanol fuel cell. In the chronoamperometry at 50ºC, the electrocatalysts with carbon (85 wt%) and ATO (15 wt%) support, showed the best activity, and the atomic proportions which achieved the best results were PtSnRh(70:25:05) e (90:05:05). PtSnRh(70:25:05)/85C+15ATO electrocatalysts showed the best performance in a direct ethanol fuel cell.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2013-08-28
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.