Tesis Doctoral
DOI
10.11606/T.85.2013.tde-29042013-095446
Documento
Autor
Nombre completo
Amanda Abati Aguiar
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2013
Director
Tribunal
Braga, Francisco Jose Correa (Presidente)
Fernandes, Stela Maria de Carvalho
Ribeiro, Christiane
Rossi, Wagner de
Salvador, Vera Lucia Ribeiro
Título en portugués
Avaliação do recobrimento biomimétrico em compósitos de alumina-zircônia texturizadas superficialmente com laser de femtossegundo
Palabras clave en portugués
alumina-zircônia
laser de femtossegundo
recobrimento biomimético
SBF
texturização superficial
Resumen en portugués
O principal objetivo deste trabalho foi estudar a influência do tratamento superficial com laser de femtossegundo em amostras de alumina e compósito de alumina-zircônia estabilizada com ítria para depósito e aderência de apatita. Os resultados obtidos mostraram que houve a formação de apatita sobre as superfícies das amostras que foram texturizadas com laser de femtossegundo e em seguida imersa em 1,5 SBF. Este método biomimético pôde, por conseguinte, tornar estas cerâmicas bioativas. Também houve a formação de apatita na superfície das amostras sem o tratamento a laser. Os efeitos da texturização na superfície para as diferentes cerâmicas e a influência do tempo de imersão em 1,5 SBF são discutidos, a fim de determinar a condição ótima para estimular a deposição e a adesão da apatita na superfície dos materiais. Finalmente, os resultados obtidos das diferentes análises são comparados. A adesão da hidroxiapatita é essencial para interação com o substrato e depende das propriedades das superfícies dos materiais. A qualidade desta adesão influenciará sua morfologia e a capacidade futura de osseointegração. As características de superfície dependem da química de superfície, energia de superfície e topografia de superfície. Geralmente, a reatividade de superfície e energia de superfície pode ser influenciada pelas características de molhabilidade, influenciando o desempenho de biomateriais. A adesão e crescimento da apatita depositada também é função da rugosidade superficial. O tratamento superficial com laser de femtossegundo melhora consideravelmente a adesão da apatita obtida pelo recobrimento biomimético nas superfícies dos materiais.
Título en inglés
Evaluation of biomimetic coating in zirconia-alumina composite textured surface with femtosecond laser
Palabras clave en inglés
alumina-zirconia
biomimetic coating
femtosecond laser
SBF
surface texturing
Resumen en inglés
The main objective of this work was to study the influence of femtosecond laser surface treatment on samples of alumina and composite of zirconia-alumina yttria stabilized for deposit and adhesion of apatite. The results showed that there was apatite formation on the surfaces of the samples that have been textured with femtosecond laser and then immersed in SBF 1.5. This biomimetic method can therefore make these bioactive ceramics. There was also the formation of apatite in the samples without laser treatment. The effects of texturing surface for the different ceramics and the influence of immersion time in SBF 1.5 are discussed in order to determine the optimal conditions to promote the deposition and the adhesion of the apatite in the material`s surface. Finally, the results of the different analyzes are compared. The adhesion of hydroxyapatite is essential for interaction with the substrate and depends on the properties of material´s surface. The quality of this adhesion will influence their morphology and the future ability of osseointegration. The surface characteristics depend on the surface chemical, surface energy and surface topography. Generally, the reactivity of surface and the energy of surface can be affected by wetting characteristics influencing the performance of biomaterials. The adhesion and growth of apatite deposited is also a function of surface roughness. The femtosecond laser surface treatment greatly improves the adhesion of apatite obtained by biomimetic coating on the surfaces of materials.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2013-06-06
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2019. Todos los derechos reservados.