Doctoral Thesis
DOI
10.11606/T.85.2013.tde-29052013-094946
Document
Author
Full name
Tamiye Simone Goia
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2013
Supervisor
Committee
Bressiani, Ana Helena de Almeida (President)
Allegrini Junior, Sergio
Higa, Olga Zazuco
Takiishi, Hidetoshi
Zavaglia, Cecília Amélia de Carvalho
Title in Portuguese
Implantes porosos à base de titânio, avaliação in vitro e in vivo
Keywords in Portuguese
liga Ti-13Nb-13Zr
osteointegração
porosidade
titânio
Abstract in Portuguese
O desenvolvimento de biomateriais com estrutura porosa visa permitir uma boa ancoragem biológica através do crescimento do tecido ósseo no interior dos poros, além de no caso de algumas ligas de titânio, proporcionar valores de módulo elástico semelhantes ao do osso, prevenindo assim o insucesso por reabsorção óssea na interface com o implante. O objetivo deste estudo foi avaliar o processamento de implantes porosos à base de titânio produzidos por metalurgia do pó, utilizando polímeros naturais como aditivos (albumina, amidos de arroz, batata, milho e a gelatina), e analisar a osteointegração desses implantes por ensaio in vivo. Foram obtidas, amostras de titânio comercialmente puro (Ticp) e da Liga Ti-13Nb-13Zr pelos processos de space-holder e suspensão; os polímeros naturais foram removidos termicamente (350°C/1h) previamente a sinterização (1300°C/1h e 1300°C/3h, respectivamente). As metodologias de processamento utilizando aditivos de baixo custo propiciaram a obtenção de implantes metálicos porosos de maneira simplificada, com porosidades diferenciadas, boa homogeneidade estrutural, grau de porosidade adequado (entre 40% e 60%), distribuição e tamanho dos poros conforme o polímero natural formador. Na caracterização biológica, o teste in vitro de citotoxicidade validou a utilização dos implantes para a realização do teste in vivo. A avaliação da osteointegração foi realizada em coelhos da raça New Zealand em períodos de 49 dias. Na análise histológica por microscopia eletrônica de varredura e fluorescência, foram obtidos os resultados quantitativos e qualitativos da osteointegração, com crescimento ósseo em todos os implantes, apresentando osteocondutividade. Os melhores resultados ocorreram em implantes com porosidade homogênea, e com tamanho médio de poros entre 100 e 200 μm. Assim, os materiais porosos de titânio e da liga Ti-13Nb-13Zr produzidos com os polímeros naturais (amido de arroz, amido de batata, amido de milho, gelatina e albumina), permitiram a nutrição e manutenção necessárias para a sobrevivência das células, comprovando a osteointegração e osteocondução dos implantes desenvolvidos.
Title in English
Titanium based porous implants, in vitro and in vivo evaluation
Keywords in English
osseointegration
porosity
Ti-13Nb-13Zr alloy
titanium
Abstract in English
The development of biomaterials with porous structure, seeks to allow a good biological anchorage through bone tissue ingrowth within the pores, besides to propitiate elastic modulus values similar to bone, thus preventing the failure by bone resorption, on implants interface. The goals of this study was to evaluate the processing of titanium based porous implants by powder metallurgy (PM), using natural polymers as additive (rice, potato and corn starches, albumin and gelatin), and evaluate these implants osseointegration by in vivo assay. Samples were obtained of commercially pure titanium (cpTi) and Ti-13Nb-13Zr alloy by space-holder and suspension techniques; the natural polymers were removed by thermal treatment (350C/1h) prior to sintering (1300C/1h and 1300C/3h respectively). The processing methodologies using low cost additives propitiate the production of porous metallic implants in a simplified manner, with differentiated porosities, good structural homogeneity, proper porosity degree (between 40% and 60%), distribution and pore size as the related natural polymer. The biological characterization was first performed in vitro with a cytotoxicity test, which allowed the use of implants in vivo. The osseointegration evaluation was performed in New Zealand White rabbits for 49 days period. Histological analyses with scanning electron microscopy and fluorescence microscopy were obtained quantitative and qualitative results of osseointegration, with bone growth in all implants, presenting osteoconductivity. The best results were in implants with homogenous porosity and with mean pore size between 100 and 200 μm. Thus, titanium and Ti-13Nb-13Zr alloy porous materials produced with natural polymers (rice, potato and corn starches, albumin and gelatin), allowed the nutrition and nourishing needed to bone cells survival, proving the osseointegration and osteoconduction features of developed implants.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
2013GoiaImplantes.pdf (12.22 Mbytes)
Publishing Date
2013-06-06
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2020. All rights reserved.