Disertación de Maestría
DOI
10.11606/D.85.2011.tde-31102011-084235
Documento
Autor
Nombre completo
Júlio Nandenha
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2011
Director
Tribunal
Linardi, Marcelo (Presidente)
Miranda Junior, Pedro
Spinacé, Estevam Vitorio
Título en portugués
Desenvolvimento de novos sistemas de eletrocatalisadores nano-dispersos 20%Pt-(2% Pt-Ce0,9W0,102)/C tolerantes ao monóxido de carbono( CO) para ânodos de PEMFC
Palabras clave en portugués
eletrocatalisadores
PEMFC
tolerância ao CO
Resumen en portugués
O material (pó) de nanofase de Ce0,9W0,1O2 foi sintetizado por coprecipitação de oxalatos de cério (IV) e cátions de tungstênio (IV). A redução da platina (2%) foi feita pelo método da redução por álcool, utilizando uma solução de ácido hexacloroplatínico (H2PtCl6.6H2O) como fonte do metal, óxido de cério dopado com tungstênio (Ce0,9W0,1O2) utilizado como suporte e, uma solução de etilenoglicol/água (75/25, v/v) como solvente e agente redutor. Os materiais 2%Pt-Ce0,9W0,1O2 foram misturados em Pt/C E-TEK 20%, utilizando-se processo de mistura física para produzir os eletrocatalisadores de 20%Pt-(2%Pt-Ce0,9W0,1O2)/C. Os eletrocatalisadores obtidos foram caracterizados por espectroscopia de energia dispersiva de raios X (EDX) acoplado à microscopia eletrônica de varredura (MEV), análises de difração de raios X (DRX), e microscopia eletrônica de transmissão (MET). O conjunto eletrodos-membrana (MEAs) foram preparados para o ânodo com cargas iguais a 0,401, 0,364, 0,328 mg Pt cm-2 de eletrocatalisadores 20%Pt-(2%Pt-Ce0,9W0,1O2)/C produzidos. No cátodo foi usada uma carga de 0,4 mg Pt cm-2 de eletrocatalisador Pt/C ETEK. A polarização anódica foi realizada para oxidação de H2/CO (100 ppm de CO). A tolerância ao CO foi estudada utilizando o processo eletroquímico (stripping de CO e medidas de curvas de polarização). Os resultados obtidos mostraram que a oxidação de CO adsorvido a CO2 na superfície de platina ocorre em potenciais menos positivos mostrando tolerância ao CO adsorvido nestes eletrocatalisadores (20%Pt-(2%Pt-Ce0,9W0,1O2)/C (50:50, 60:40 e 70:30)) a uma temperatura de 85 ºC e com pressão absoluta de 2 bar para ânodo e cátodo, comparado com Pt/C E-TEK 20%.
Título en inglés
Development of new systems of nano-disperse 20%Pt-(2%Pt-Ce0,9W0,1O2)/C electrocatalysts tolerant to carbon monoxide (CO) for PEMFCs anodes
Palabras clave en inglés
CO tolerance
electrocatalysts
PEMFC
Resumen en inglés
The nanophase material (powder) of Ce0,9W0,1O2 was synthesized via coprecipitation of oxalates of cerium (IV) and tungsten cations. The reduction of platinum (2%) was made by the method of alcohol reduction, using an acid solution hexachloroplatinic (H2PtCl6.6H2O) as metal source, cerium oxide doped with tungsten (Ce0,9W0,1O2) used as support and the solution of ethylene glycol/water (75/75, v/v) as solvent and reducing agent. The 2%Pt-Ce0,9W0,1O2 materials were mixed in Pt/C E-TEK 20% using physical mixing process to produce the 20%Pt-(2%Pt-Ce0,9W0,1O2)/C electrocatalyst. The materials were characterized by energy dispersive X-ray spectroscopy (EDX) coupled to scanning electron microscopy (SEM), X-ray difratometry analysis (XRD) and transmission electronic microscopy (TEM). The membrane electrodes assembly (MEAs) were prepared with loads equal to 0.401, 0.364, 0.328 mg Pt cm-2 for 20%Pt(2%Pt-Ce0,9W0,1O2)/C electrocatalysts produced. In the cathode a load of 0.4 mg Pt cm-2 of commercial Pt/C ETEK electrocatalyst was used. The anodic polarization was carried out for oxidation of the mixture H2/CO(100 ppm CO). The CO tolerance was studied using electrochemical process (CO stripping and measurements of polarization curves). The results showed that the oxidation of CO adsorbed to CO2 on the surface of platinum occur at less positive potentials showing tolerance to CO adsorbed on these 20%Pt-(2%Pt-Ce0,9W0,1O2)/C (50:50, 60:40 and 70:30) electrocatalysts at a temperature of 85 ºC and absolute pressure of 2 bar for anode and cathode, compared with Pt/C E-TEK 20%.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2011-12-14
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.