Mémoire de Maîtrise
DOI
10.11606/D.85.2011.tde-31102011-084235
Document
Auteur
Nom complet
Júlio Nandenha
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2011
Directeur
Jury
Linardi, Marcelo (Président)
Miranda Junior, Pedro
Spinacé, Estevam Vitorio
Titre en portugais
Desenvolvimento de novos sistemas de eletrocatalisadores nano-dispersos 20%Pt-(2% Pt-Ce0,9W0,102)/C tolerantes ao monóxido de carbono( CO) para ânodos de PEMFC
Mots-clés en portugais
eletrocatalisadores
PEMFC
tolerância ao CO
Resumé en portugais
O material (pó) de nanofase de Ce0,9W0,1O2 foi sintetizado por coprecipitação de oxalatos de cério (IV) e cátions de tungstênio (IV). A redução da platina (2%) foi feita pelo método da redução por álcool, utilizando uma solução de ácido hexacloroplatínico (H2PtCl6.6H2O) como fonte do metal, óxido de cério dopado com tungstênio (Ce0,9W0,1O2) utilizado como suporte e, uma solução de etilenoglicol/água (75/25, v/v) como solvente e agente redutor. Os materiais 2%Pt-Ce0,9W0,1O2 foram misturados em Pt/C E-TEK 20%, utilizando-se processo de mistura física para produzir os eletrocatalisadores de 20%Pt-(2%Pt-Ce0,9W0,1O2)/C. Os eletrocatalisadores obtidos foram caracterizados por espectroscopia de energia dispersiva de raios X (EDX) acoplado à microscopia eletrônica de varredura (MEV), análises de difração de raios X (DRX), e microscopia eletrônica de transmissão (MET). O conjunto eletrodos-membrana (MEAs) foram preparados para o ânodo com cargas iguais a 0,401, 0,364, 0,328 mg Pt cm-2 de eletrocatalisadores 20%Pt-(2%Pt-Ce0,9W0,1O2)/C produzidos. No cátodo foi usada uma carga de 0,4 mg Pt cm-2 de eletrocatalisador Pt/C ETEK. A polarização anódica foi realizada para oxidação de H2/CO (100 ppm de CO). A tolerância ao CO foi estudada utilizando o processo eletroquímico (stripping de CO e medidas de curvas de polarização). Os resultados obtidos mostraram que a oxidação de CO adsorvido a CO2 na superfície de platina ocorre em potenciais menos positivos mostrando tolerância ao CO adsorvido nestes eletrocatalisadores (20%Pt-(2%Pt-Ce0,9W0,1O2)/C (50:50, 60:40 e 70:30)) a uma temperatura de 85 ºC e com pressão absoluta de 2 bar para ânodo e cátodo, comparado com Pt/C E-TEK 20%.
Titre en anglais
Development of new systems of nano-disperse 20%Pt-(2%Pt-Ce0,9W0,1O2)/C electrocatalysts tolerant to carbon monoxide (CO) for PEMFCs anodes
Mots-clés en anglais
CO tolerance
electrocatalysts
PEMFC
Resumé en anglais
The nanophase material (powder) of Ce0,9W0,1O2 was synthesized via coprecipitation of oxalates of cerium (IV) and tungsten cations. The reduction of platinum (2%) was made by the method of alcohol reduction, using an acid solution hexachloroplatinic (H2PtCl6.6H2O) as metal source, cerium oxide doped with tungsten (Ce0,9W0,1O2) used as support and the solution of ethylene glycol/water (75/75, v/v) as solvent and reducing agent. The 2%Pt-Ce0,9W0,1O2 materials were mixed in Pt/C E-TEK 20% using physical mixing process to produce the 20%Pt-(2%Pt-Ce0,9W0,1O2)/C electrocatalyst. The materials were characterized by energy dispersive X-ray spectroscopy (EDX) coupled to scanning electron microscopy (SEM), X-ray difratometry analysis (XRD) and transmission electronic microscopy (TEM). The membrane electrodes assembly (MEAs) were prepared with loads equal to 0.401, 0.364, 0.328 mg Pt cm-2 for 20%Pt(2%Pt-Ce0,9W0,1O2)/C electrocatalysts produced. In the cathode a load of 0.4 mg Pt cm-2 of commercial Pt/C ETEK electrocatalyst was used. The anodic polarization was carried out for oxidation of the mixture H2/CO(100 ppm CO). The CO tolerance was studied using electrochemical process (CO stripping and measurements of polarization curves). The results showed that the oxidation of CO adsorbed to CO2 on the surface of platinum occur at less positive potentials showing tolerance to CO adsorbed on these 20%Pt-(2%Pt-Ce0,9W0,1O2)/C (50:50, 60:40 and 70:30) electrocatalysts at a temperature of 85 ºC and absolute pressure of 2 bar for anode and cathode, compared with Pt/C E-TEK 20%.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2011-12-14
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.