Disertación de Maestría
DOI
10.11606/D.85.2010.tde-31102011-090400
Documento
Autor
Nombre completo
Marcos Gonzales Fernandes
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2010
Director
Tribunal
Rossi, Jesualdo Luiz (Presidente)
Mucsi, Cristiano Stefano
Padilha, Angelo Fernando
Título en portugués
Obtenção de fios em ligas cobre-magnésio para utilização em linhas de transmissão de energia elétrica
Palabras clave en portugués
condutividade elétrica
forno a arco elétrico
forno resistivo
fusão
ligas de cobre
Resumen en portugués
O objetivo desse trabalho foi o de obter-se fios de cobre em três composições químicas distintas da liga Cu-Mg a partir de cobre eletrolítico e de magnésio. Foram avaliadas as etapas envolvidas, começando com a fusão de botões em forno a arco na composição do eutético Cu-Mg, diluição destes botões em forno resistivo, vazamento em lingoteira de cobre, seguido de tratamento térmico de homogeneização em forno resistivo a 910 ºC por 2 h. Os tarugos foram posteriormente trabalhados mecanicamente por forjamento rotativo seguido de um passe final de acabamento por trefilação, para obtenção do fio. As análises químicas realizadas nos lingotes indicaram que a rota de preparação dos fios mostrou-se adequada aos estudos em escala de laboratório, suficiente para a confecção de fios com área de seção transversal de 4 mm2 por 10 m de comprimento, para cada composição de liga. Os fios foram caracterizados mecanicamente por ensaio de tração e de dureza após tratamento térmico de recristalização a 510 ºC por 1 h. Os fios também tiveram as condutividades elétricas medidas na condição recristalizada e os resultados foram comparados com dados experimentais da literatura. Os materiais obtidos mostraram-se adequados à utilização como fio condutor de energia elétrica. Os limites de escoamento e de resistência a tração tiveram seus valores melhorados com o aumento do teor de magnésio na liga, 11 % e 24 %, respectivamente, enquanto houve queda nos valores de condutividade elétrica para cerca de 60 % IACS (International Annealed Copper Standard).
Título en inglés
Obtention of copper-magnesium alloys wires used in eletrical transmission lines
Palabras clave en inglés
copper alloys
electric arc furnace
electrical conductivity
melting
resistive furnace
Resumen en inglés
The aim of this work was to obtain copper wires in three different chemical compositions starting from electrolytic copper and magnesium. The mains steps were evaluated, starting from the melting of small eutectic cooper-magnesium specimens in an electric arc furnace, followed by further dilution of this buttons in a resistive furnace and casting it in a copper mould. The as cast billets were homogenized in a resistive furnace at 910 ºC for 2 h. The billets were mechanically cold worked by swaging and a final drawing step to attain a round shape and a reasonable surface quality. The cast ingots chemical analysis indicated that the processing route showed to be adequate, in laboratory scale, to obtain wires with cross sectional area of 4 mm2 and 10 m in length. The wires in both conditions as cold worked and after a recovering heat treatment at 510 ºC for 1 h, were mechanically characterized by tensile testing and hardness. The wires had also the electric conductivity assessed in the recovered heat-treated state and the results were compared to the literature data. The obtained material showed to be adequate to be used as electric conductor. The yield strain and ultimate tensile strength were improved with the increasing amount of Mg in the alloy, 11 % and 24 %, respectively, while the electric conductivity decreased to 60 % IACS (International Annealed Copper Standard).
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2011-12-14
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.