Mémoire de Maîtrise
DOI
10.11606/D.85.2010.tde-31102011-090400
Document
Auteur
Nom complet
Marcos Gonzales Fernandes
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2010
Directeur
Jury
Rossi, Jesualdo Luiz (Président)
Mucsi, Cristiano Stefano
Padilha, Angelo Fernando
Titre en portugais
Obtenção de fios em ligas cobre-magnésio para utilização em linhas de transmissão de energia elétrica
Mots-clés en portugais
condutividade elétrica
forno a arco elétrico
forno resistivo
fusão
ligas de cobre
Resumé en portugais
O objetivo desse trabalho foi o de obter-se fios de cobre em três composições químicas distintas da liga Cu-Mg a partir de cobre eletrolítico e de magnésio. Foram avaliadas as etapas envolvidas, começando com a fusão de botões em forno a arco na composição do eutético Cu-Mg, diluição destes botões em forno resistivo, vazamento em lingoteira de cobre, seguido de tratamento térmico de homogeneização em forno resistivo a 910 ºC por 2 h. Os tarugos foram posteriormente trabalhados mecanicamente por forjamento rotativo seguido de um passe final de acabamento por trefilação, para obtenção do fio. As análises químicas realizadas nos lingotes indicaram que a rota de preparação dos fios mostrou-se adequada aos estudos em escala de laboratório, suficiente para a confecção de fios com área de seção transversal de 4 mm2 por 10 m de comprimento, para cada composição de liga. Os fios foram caracterizados mecanicamente por ensaio de tração e de dureza após tratamento térmico de recristalização a 510 ºC por 1 h. Os fios também tiveram as condutividades elétricas medidas na condição recristalizada e os resultados foram comparados com dados experimentais da literatura. Os materiais obtidos mostraram-se adequados à utilização como fio condutor de energia elétrica. Os limites de escoamento e de resistência a tração tiveram seus valores melhorados com o aumento do teor de magnésio na liga, 11 % e 24 %, respectivamente, enquanto houve queda nos valores de condutividade elétrica para cerca de 60 % IACS (International Annealed Copper Standard).
Titre en anglais
Obtention of copper-magnesium alloys wires used in eletrical transmission lines
Mots-clés en anglais
copper alloys
electric arc furnace
electrical conductivity
melting
resistive furnace
Resumé en anglais
The aim of this work was to obtain copper wires in three different chemical compositions starting from electrolytic copper and magnesium. The mains steps were evaluated, starting from the melting of small eutectic cooper-magnesium specimens in an electric arc furnace, followed by further dilution of this buttons in a resistive furnace and casting it in a copper mould. The as cast billets were homogenized in a resistive furnace at 910 ºC for 2 h. The billets were mechanically cold worked by swaging and a final drawing step to attain a round shape and a reasonable surface quality. The cast ingots chemical analysis indicated that the processing route showed to be adequate, in laboratory scale, to obtain wires with cross sectional area of 4 mm2 and 10 m in length. The wires in both conditions as cold worked and after a recovering heat treatment at 510 ºC for 1 h, were mechanically characterized by tensile testing and hardness. The wires had also the electric conductivity assessed in the recovered heat-treated state and the results were compared to the literature data. The obtained material showed to be adequate to be used as electric conductor. The yield strain and ultimate tensile strength were improved with the increasing amount of Mg in the alloy, 11 % and 24 %, respectively, while the electric conductivity decreased to 60 % IACS (International Annealed Copper Standard).
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2011-12-14
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.