Disertación de Maestría
DOI
10.11606/D.88.2010.tde-02032010-161526
Documento
Autor
Nombre completo
Leiliane Cristina Cossolino
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2010
Director
Tribunal
Zanatta, Antonio Ricardo (Presidente)
Li, Maximo Siu
Tessler, Leandro Russovski
Título en portugués
Estudo das propriedades opto-eletrônicas de micro-cristais de rubi
Palabras clave en portugués
Al2O3:Cr3+
Filmes finos
Materiais Luminescentes
Micro-estruturas de rubi
Propriedades ópticas
Resumen en portugués
Filmes amorfos de nitreto de alumínio (AlN) foram preparados por sputtering de rádio frequência convencional em um alvo de Al+Cr e plasma de nitrogênio puro. A área relativa de Al-Cr determina o conteúdo de Cr, o qual esteve em um intervalo de concentração de ~ 0 3.33 at.% no presente estudo. A deposição dos filmes foi seguida por tratamento térmico das amostras até 1050 ºC e por caracterização espectroscópica através de medidas de EDS (Energy Dispersive Spectrometry), Foto-luminescência e Transmissão Óptica. De acordo com os resultados experimentais, as propriedades óptico-eletrônicas dos filmes de AlN contendo Cr são altamente influenciadas tanto pela concentração de Cr como pela temperatura de tratamento térmico. Na verdade, o tratamento térmico a 1050 ºC induz o desenvolvimento de estruturas que, devido ao seu tamanho típico e características espectrais exclusivas, foram designadas por micro-estruturas de rubi (RbMSs). Estas RbMSs são rodeadas por um meio rico em nitrogênio no qual os íons Cr3+ apresentam características luminescentes não encontradas na literatura. A emissão de luz apresentada pelas RbMSs e suas vizinhanças foram investigadas de acordo com o conteúdo de Cr e a temperatura de medida permitindo a identificação de várias linhas luminescentes relatadas do Cr3+. As principais características destas linhas luminescentes e correspondentes processos de recombinação-excitação são apresentados e discutidos tendo em vista uma análise espectroscópica detalhada.
Título en inglés
Study of opto-electronics properties of ruby micro-crystals
Palabras clave en inglés
Al2O3:Cr3+
Luminescent Materials
Optical Properties
Ruby Microstructures
Thin Films
Resumen en inglés
Films of amorphous aluminum-nitride (AlN) were prepared by conventional radio frequency sputtering of an Al+Cr target in a plasma of pure nitrogen. The Cr-to-Al relative area determines the chromium content, which stayed in the ~ 0 3.33 at.% concentration range in the present study. Film deposition was followed by thermal annealing the samples up to 1050 ºC and by spectroscopic characterization through energy dispersive spectrometry (EDS), Photo-luminescence and Optical Transmission measurements. According to the experimental results, the optical-electronic properties of the Cr-containing AlN films are highly influenced by both the Cr concentration and the temperature of the thermal treatments. In fact, thermal annealing at 1050 °C induces the development of structures which, because of their typical size and unique spectral characteristics, were designated by ruby microstructures (RbMS's). These RbMS's are surrounded by a nitrogen-rich environment in which Cr3+ ions exhibit luminescent features with no counterpart in the literature. The light emission presented by the RbMS's and surroundings were investigated according to the Cr content and temperature of measurement allowing the identification of several Cr3+-related luminescent lines. The main characteristics of these luminescent lines and corresponding excitation-recombination processes are presented and discussed in view of a detailed spectroscopic analysis.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2010-03-04
 
ADVERTENCIA: El material descrito abajo se refiere a los trabajos derivados de esta tesis o disertación. El contenido de estos documentos es responsabilidad del autor de la tesis o disertación.
  • COSSOLINO, L C, and ZANATTA, A R. Influence of chromium concentration on the optical–electronic properties of ruby microstructures [doi:10.1088/0022-3727/43/1/015302]. Journal of Physics D: Applied Physics [online], 2010, vol. 43, n. 1, p. 015302.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.