Disertación de Maestría
DOI
10.11606/D.88.1998.tde-02072003-093007
Documento
Autor
Nombre completo
André Luís Paschoal
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1998
Director
Tribunal
Canale, Lauralice de Campos Franceschini (Presidente)
Andreeta, Jose Pedro
Higa, Olga Zazuco
Título en portugués
Avaliação da resistência à corrosão em meio fisiológico de metais revestidos com nitreto de titânio.
Palabras clave en portugués
biomateriais metálicos
nitreto de titânio
revestimento
Resumen en portugués
Metais são bastante usados como materiais implantáveis, principalmente para dispositivos feitos na área de ortopedia. Há uma constante relação dos processos de corrosão nesse biomateriais com a agressividade do meio fisiológico. Usando quatro tipo de metais e ligas metálicas – titânio puro, liga de titânio, aço inoxidável de baixo carbono e liga de cobalto – o processo de corrosão foi estudado. Além disso, o desempenho desses materiais revestidos com nitreto de titânio foi avaliado. Dois processos de revestimento por PVD – evaporação e magnetron sputtering – foram executados, verificando a eficiência desses materiais em meio fisiológico - O melhor comportamento se deu para o revestimento obtido por evaporação. O mecanismo de corrosão predominante para as amostras foi indicado.
Título en inglés
Evaluation of the resistance to the corrosion in physiologic environment of metals covered with titanium nitrite.
Palabras clave en inglés
coating
metallic biomaterials
titanium nitrite
Resumen en inglés
Metals are very much used as implantable materials mainly for the construction of devices orthopaedic area. There is a constant concern about the corrosion process in those metallic biomaterials due to the aggressiveness of the physiological environment. By using four types of metals and metallic alloys – pure titanium, titanium alloy, low carbon stainless steel and cobalt-chromium alloy – the corrosion process in physiologic environment has been studied. Also, the performance of such materials coated with titanium nitrate was evaluated. Two PVD coating methods – evaporation and magnetron sputtering – were performed, and the efficiency of those materials in physiologic medium was verified. The best behaviour was found by the evaporation coating method. The predominant corrosion mechanism for coated samples was suggested.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
dissertandre.pdf (8.78 Mbytes)
Fecha de Publicación
2003-09-01
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.