Tesis Doctoral
DOI
10.11606/T.88.1998.tde-03052010-171319
Documento
Autor
Nombre completo
Antonio Riul Júnior
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1998
Director
Tribunal
Oliveira Junior, Osvaldo Novais de (Presidente)
Faria, Roberto Mendonça
Moreira, Wania da Conceição
Oliveira, Elisabeth Andreoli de
Zaniquelli, Maria Elisabete Darbello
Título en portugués
Filmes de Langmuir e Langmuir-Blodgett de Polianilinas
Palabras clave en portugués
Filmes Langmuir-Blodgett
Monocamadas de Langmuir
Polianilina
Resumen en portugués
Explorou-se a caracterização de monocamadas e filmes LB de polianilina (PANi), e um oligômero de polianilina, chamado aqui de 16-mero, com estearato de cádmio (CdSt). A análise dos filmes de Langmuir indicou que possivelmente não há mistura em nível molecular da PANi e do 16-mero com CdSt, ainda que a quantidade adicionada em solução de polímero ou oligômero influencie a estabilidade das monocamadas. Utilizou-se UV-vis, FTIR, difração de raios-X, condutividade elétrica, elipsometria, microscopia óptica e potencial de superficie para caracterização dos filmes LB. Os resultados de UV-vis indicaram uma transferência uniforme e ainda que os filmes recém depositados encontram-se desdopados. A análise de FTIR confirma a presença de CdSt nos filmes LB, e o efeito de desdopagem em subfases neutras, corroborando os resultados de UV-vis. A difração de raios-X indica a presença de domínios separados de PANi (e 16-mero) com CdSt nos filmes LB. Resultados elipsométricos indicaram uma espessura por camada em tomo de 25 Å. A excelente uniformidade obtida nos filmes LB mistos foi comprovada pelos resultados de microscopia óptica e potencial de superficie. Esses filmes mistos apresentaram valores de condutividade elétrica em tomo de 10-4 a 10-5 S.cm-1 (van der Pauw), tanto para a PANi quanto para o 16-mero. Investigou-se também o efeito da exposição dos filmes mistos PANi/CdSt aos raios-X. Nota-se um deslocamento para a região do vermelho, na região do visível, nos espectros de UVvis, similar à observada pela dopagem através de ácidos inorgânicos. Verificou-se que os efeitos de umidade da atmosfera de medida são predominantes nesse processo de dopagem. É feita uma análise dos resultados de condutividade elétrica, comparando-os com os encontrados na literatura.
Título en inglés
Langmuir and Langmuir-Blodgett films of polyaniline.
Palabras clave en inglés
Lagmuir-Blodgett films
Langmuir monolayers
Polyaniline
Resumen en inglés
A study has been made of composite Langmuir and Langmuir-Blodgett (LB) films of polyaniline (PANi), and a polyaniline oligomer (l6-mer polyaniline), with cadmium stearate (CdSt). The monolayers studies pointed to a phase separated system containing the polymer (or the 16-mer) and CdSt, with no mixing at the molecular leveI, although the relative contents of PANi and 16-mer in the solution have a strong influence on the monolayer stability. UV-vis, FTIR, X-ray difIraction (XRD), electrical conductivity, ellipsometry, optical microscopy and surface potential measurements were used in the LB film characterization. UV-vis results have shown a uniform transfer, with the as deposited films in the undoped state. FTIR results confirmed the presence of CdSt and undoped polyaniline (and 16-mer) in the transferred LB films, corroborating the UV-vis results. XRD has shown separated domains of CdSt and PANi (l6-mer also) in the LB films. Ellipsometry data indicated a thickness of 25 Å per deposited layer. The high uniformity in these mixed LB films was confirmed by optical microscopy and surface potential measurements. The electrical conductivity was approximately 10-4 to 10-5 S.cm-1 for both PANi and 16-mer. Mixed PANi/CdSt films were also exposed to X-ray irradiation. After a given dose rate there is a red shift in the UV-vis spectra from the 600 nm region to the 800 nm region, similar to the usual acid doping process observed in polyaniline. Humidity effects have a strong influence on the doping process. A comparison is made of the conductivity measurements made here with those reported in the literature.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
AntonioRiulJrD.pdf (2.04 Mbytes)
Fecha de Publicación
2010-05-13
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.