Disertación de Maestría
DOI
10.11606/D.88.2005.tde-04012011-141307
Documento
Autor
Nombre completo
Diego José Inforzato
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2005
Director
Tribunal
Spinelli, Dirceu (Presidente)
Milan, Marcelo Tadeu
Tokimatsu, Ruis Camargo
Título en portugués
Estudo do comportamento dos aços ferramenta Thyrotherm 2999 EFS supra e H13 sob fadiga de baixo ciclo a altas temperaturas
Palabras clave en portugués
Aços ferramenta
Fadiga de baixo ciclo e altas temperaturas
Modelo de previsão
Modelo estimativo
Vida
Resumen en portugués
Realizou-se neste trabalho uma investigação comparativa do comportamento dos aços ferramenta H13 e THYROTHERM 2999 EFS SUPRA, destinados à fabricação de matrizes para conformação a quente, quando submetidos à fadiga de baixo ciclo a altas temperaturas (FBCAT). A partir de suas curvas de revenimento, foram definidas três durezas de trabalho para cada material (durezas de 42, 52 e 58 HRC), correspondendo a três temperaturas de revenimento distintas e três condições de estudo, buscando-se a condição ótima apresentada por estes materiais para este tipo de aplicação, visando-se então analisar a influência da dureza inicial do material na vida do componente. Foi determinada também a temperatura de ensaio de fadiga isotérmica, em 400°C, correspondente à temperatura de utilização da matriz, ou seja, uma temperatura crítica típica que a matriz atinge durante a solicitação em trabalho. A seguir foram realizados para cada material os ensaios de tração a temperatura ambiente, e na seqüência, os ensaios de tração na temperatura de trabalho definida, que permitiram a determinação dos primeiros parâmetros monotônicos dos materiais, dentre eles uma previsão para os níveis de deformação a serem utilizados nos ensaios de fadiga (0.5,0.6,0.7,0.8,0.9,1.0 e 1.1%), e demais parâmetros como E, k, n, σe, σ’f, ε’f, b, c, que permitiram a elaboração de curvas ε−N, com um modelo estimativo já existente. Finalmente, foram então realizados os ensaios de fadiga isotérmica de baixo ciclo, à temperatura de 400°C, e os resultados foram utilizados para a elaboração das curvas ε−N, resultando então na proposta de um modelo de previsão de resistência à fadiga específico para os materiais pesquisados.
Título en inglés
Evaluation of Thyrotherm 2999 EFS supra and H13 tool steels, under low cycle fatigue, at higher temperature
Palabras clave en inglés
Estimating model
High temperature low cycle fatigue
Life
Prediction model
Tool steels
Resumen en inglés
It was made in this work an investigative comparison of the behavior of the tool steels H13 and THYROTHERM 2999 EFS SUPRA, designed for die steels for hot forming, when exposed to high temperature low cycle fatigue (HTLCF). From their tempering curves three material working hardness were defined for each material (hardness of 42, 52 and 58 HRC), corresponding to three different tempering temperatures, and so three study cases for each material, searching for the best condition for this kind of application, and to assess the influence of the initial hardness on the part material life. The isothermal low cycle fatigue test temperature was either defined at 400°C, corresponding to the used temperature at the die steel, i.e., a critical typical temperature that the forging dies reach on hot working. After that, tensile tests were performed for both materials, at room temperature, and at the working temperature formerly defined, and these tests allowed the definition of the first monotonic parameters for these materials, among them predictions for strain levels (0.5, 0.6, 0.7, 0.8, 0.9, 1.0 and 1.1%), to be used on fatigue tests, and further parameters like E, k, n, σe, σ’f, ε’f, b, c, that allowed the elaboration of ε−N curves, based on a still existing prediction model. Finally, isothermal low cycle fatigue tests were performed, at 400°C, and the results were used for ε−N curves elaboration, resulting on a prediction model of the fatigue strength specified for the assessed materials.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2011-01-07
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.