Tesis Doctoral
DOI
Documento
Autor
Nombre completo
Jorge Tomioka
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1999
Director
Tribunal
Giacometti, Jose Alberto (Presidente)
Biscegli, Clovis Isberto
Ferreira, Guilherme Fontes Leal
Scarpa, Paulo Cesar do Nascimento
Zilio, Sergio Carlos
Título en portugués
Técnica do Pulso Eletroacústico para medidas de Perfis de Carga Espacial em Dielétricos
Palabras clave en portugués
cabos subterrâneos
carga espacial
isolação elétrica
materiais dielétricos
polietileno
pulso eletroacústico
Resumen en portugués
Neste trabalho descreve-se a implementação da técnica do pulso eletroacústico (PEA) para a determinação de perfis de carga espacial em dielétricos. O método é baseado no sinal acústico gerado pela aplicação de um pulso de tensão elétrica de curta duração na amostra. O sinal acústico gerado é detectado usando-se um transdutor piezoelétrico acoplado à amostra. São discutidos os detalhes experimentais do sistema e os procedimentos matemáticos para o tratamento do sinal elétrico medido. O tratamento matemático do sinal é baseado na técnica de desconvolução que permite determinar a função de transferência do sistema. A função de transferência permite eliminar do sinal medido as distorções introduzidas pelo circuito de medida, pelas reflexões espúrias do sinal acústico, etc.. Mostra-se também os procedimentos matemáticos para se corrigir a atenuação e dispersão do sinal acústico durante a propagação através da amostra. A técnica PEA foi utilizada para o estudo dos perfis de carga espacial injetada em amostras de polietileno sintetizados com diferentes catalisadores: Ziegler-Natta e Metallocene. O campo elétrico aplicado para polarizar as amostras e injetar cargas elétricas nas amostras foi variado de 0,05 MV/cm a 0,9 MV/cm. Nas amostras de polietileno sem aditivos a injeção de cargas elétricas na amostra é bem menor que em amostras com aditivos anti-oxidantes Mostra-se também que o campo elétrico de ruptura depende da carga injetada na amostra, sendo ele maior quando a polaridade da tensão de teste de ruptura é a mesma da tensão aplicada que provocou a injeção de cargas elétricas na amostra.
Título en inglés
Electro-acoustic Pulse to Measure Space Charge Profile in Dielectric Materials
Palabras clave en inglés
dielectric material
electroacoustic pulse
insulated cable
polyethylene
space charge
underground power cable
Resumen en inglés
It is described the implementation of the electroacustic pulse technique, PEA, for the determination of space charge profiles in dielectrics. The method is based on the acoustic signal generated by the application of a voltage pulse with short duration on the sample. The acoustic signal generated by pulse is detected by using a piezoelectric transducer coupled to the sample. Details of the experimental system and of the mathematical procedure for the treatment of the measured electric signals are discussed. The mathematical treatment is based on the deconvolution technique which enables us to obtain the transference function of the system. The use of a transference function eliminates distortions caused by reflections that are introduced by the measurement circuit. Mathematical procedures for the correction of attenuation and dispersion of the acoustic signal during the propagation throughout the sample are also discussed. The PEA technique was used to measure the profiles of injected space charge in polyethylene synthesized using different catalysts: Ziegler-Natta and Metallocene. The electric field applied to polarize and to inject electric charges in the sample was varied form 0.05MV/cm to 0.9MV/cm. In samples of polyethylene without additives it was observed that the injection of charges is less intense than in samples containing anti oxidant additives. It is also shown that the critical electric field for the breakdown depends on the injected charge on the sample being; larger if the rupture tests were performed using the same polarity of the voltage used to pole the samples. Breakdown measurements were also performed with ozone treated samples.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
tesetomioka.pdf (1.72 Mbytes)
Fecha de Publicación
2004-04-30
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.