Disertación de Maestría
DOI
10.11606/D.88.2003.tde-05122014-172440
Documento
Autor
Nombre completo
Marcos Aurélio Viatroski
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2003
Director
Tribunal
Cruz, Gerson Kniphoff da (Presidente)
Gonzalez, Jose Pedro Donoso
Ribeiro, Sidney José Lima
Título en portugués
Análise espectroscópica do sistema vítreo ZBLAN: Er3+ em baixa temperatura
Palabras clave en portugués
Espectroscopia
ZBLAN:Er3+
Resumen en portugués
Vidros dopados com íons de elementos terras−raras são amplamente estudados com o objetivo de obtenção de meios ativos para lasers, amplificadores e sensores ópticos. Dentro desta classe de materiais, o vidro ZBLAN dopado com íons de Er+3, tem recebido grande atenção nos últimos anos. No entanto, nenhum estudo em espectroscopia óptica foi realizado para este sistema vítreo (ZBLAN:Er3+) em temperaturas inferiores a 10 K. Nesta dissertação foi promovida com sucesso, através de medidas de absorção, e luminescência entre os multipletos 4S3⁄2 e 4I15⁄2, uma completa identificação experimental das posições dos níveis de energia dos multipletos excitado (4S3⁄2) e fundamental (4I15⁄2), do íon Er3+,na matriz ZBLAN na temperatura de 2 K. Os resultados obtidos e aqui apresentados são inéditos e indicam a ocupação de sítios muito semelhantes pelos íons Er3+ dentro da matriz vítrea. Também a partir da comparação entre o espectro de luminescência e conversão ascendente de energia foi possível observar um forte acoplamento entre os íons Er3+ e a matriz ZBLAN
Título en inglés
Spectroscopy analysis of the ZBLAN system: Er3+ at low temperature
Palabras clave en inglés
Spectroscopy
ZBLAN:Er3+
Resumen en inglés
Glasses doped with earth−rare elements ions are widely study with the objective of obtains of the active environment for lasers, optics amplifier and optics feeler. Inside this material c1ass, the ZBLAN glass doped with Er3+ ions has received great attention on last years. Meantime, either study in optic spectroscopy ware realized for this system (ZBLAN:Er3+) in temperature below 10 K. In this paper was realized with success, through measures of absorption and luminescence between 4S3⁄2 e 4I15⁄2 multiplets, a complete experimental identification of the stark positions for 4S3⁄2 and 4I15⁄2 multiplets, for Er3+ ions, in ZBLAN glass matrix at 2 K. The resultants obtained here are originals and showed the occupation of environment very similar by Er3+ ions. To finish we show from the comparison between the luminescence and ascendant conversion of energy spectrum was possible observe the existence of an interaction strong between the ZBLAN glass matrix with Er3+ ions.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2014-12-08
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.