Disertación de Maestría
DOI
Documento
Autor
Nombre completo
Manoel Gregorio de Miranda Filho
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1999
Director
Tribunal
Giacometti, José Alberto (Presidente)
Eiras, José Antonio
Malmonge, José Antonio
Título en portugués
Determinação do coeficiente piroelétrico de polímeros utilizando a técnica de temperatura oscilante no tempo
Palabras clave en portugués
Ferroeletricidade
Piroeletricidade
Polarização elétrica
Resumen en portugués
O objetivo deste trabalho foi implementar um sistema para a determinação do coeficiente piroelétrico em materiais poliméricos. O método consiste em variar a temperatura da amostra de forma senoidal e medir a corrente em função do tempo. Através do sinal da corrente elétrica e da sua diferença de fase com a temperatura, separa-se a corrente elétrica de origem piroelétrica, a partir da qual se determina o coeficiente piroelétrico. Apresenta-se a caracterização do sistema abrangendo aspectos como o intervalo de temperatura das medidas e amplitude e freqüência da oscilação da temperatura. O método foi empregado para realizar medidas exploratórias com o polímero ferroelétrico poli(fluoreto de vinilideno), PVDF, polarizado pela aplicação de uma rampa de tensão, e com o polímero poli(metacrilato de metila), PMMA, com corante polar, polarizado com o triodo de corona. Nas medidas foram variados os parâmetros do processo de polarização elétrica tais como o campo elétrico máximo e a temperatura
Título en inglés
Pyroelectric coefficient determination of polymers using sinusoidal temperature variation technique
Palabras clave en inglés
Electric polarization
Ferroelectricity
Pyroelectricity
Resumen en inglés
An experimental setup to measure the pyroelectric coefficient of polymers was implemented. The method is based on the measurement of the electric current generated by the sample when its temperature was set to oscillate sinusoidally. Using the measured current and its phase difference related with the temperature thepyroelectric current was obtained, from that the pyroelectric coefficient was determined. It is shown the characterization of the experimental system such as the temperature amplitude and frequency interval of operation. The method was applied in exploratory measurements employing the ferroelectric polymer poly(vynilidene fIuoride), PVDF, poled by a ramp voltage, and the poly(methyl metacrylate), PMMA, having a polar dye, poled with the carona triode. Measurements were performed far different poling conditions such as the maximum applied field and temperature
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2014-12-08
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.