Dissertação de Mestrado
DOI
Documento
Autor
Nome completo
Manoel Gregorio de Miranda Filho
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Carlos, 1999
Orientador
Banca examinadora
Giacometti, José Alberto (Presidente)
Eiras, José Antonio
Malmonge, José Antonio
Título em português
Determinação do coeficiente piroelétrico de polímeros utilizando a técnica de temperatura oscilante no tempo
Palavras-chave em português
Ferroeletricidade
Piroeletricidade
Polarização elétrica
Resumo em português
O objetivo deste trabalho foi implementar um sistema para a determinação do coeficiente piroelétrico em materiais poliméricos. O método consiste em variar a temperatura da amostra de forma senoidal e medir a corrente em função do tempo. Através do sinal da corrente elétrica e da sua diferença de fase com a temperatura, separa-se a corrente elétrica de origem piroelétrica, a partir da qual se determina o coeficiente piroelétrico. Apresenta-se a caracterização do sistema abrangendo aspectos como o intervalo de temperatura das medidas e amplitude e freqüência da oscilação da temperatura. O método foi empregado para realizar medidas exploratórias com o polímero ferroelétrico poli(fluoreto de vinilideno), PVDF, polarizado pela aplicação de uma rampa de tensão, e com o polímero poli(metacrilato de metila), PMMA, com corante polar, polarizado com o triodo de corona. Nas medidas foram variados os parâmetros do processo de polarização elétrica tais como o campo elétrico máximo e a temperatura
Título em inglês
Pyroelectric coefficient determination of polymers using sinusoidal temperature variation technique
Palavras-chave em inglês
Electric polarization
Ferroelectricity
Pyroelectricity
Resumo em inglês
An experimental setup to measure the pyroelectric coefficient of polymers was implemented. The method is based on the measurement of the electric current generated by the sample when its temperature was set to oscillate sinusoidally. Using the measured current and its phase difference related with the temperature thepyroelectric current was obtained, from that the pyroelectric coefficient was determined. It is shown the characterization of the experimental system such as the temperature amplitude and frequency interval of operation. The method was applied in exploratory measurements employing the ferroelectric polymer poly(vynilidene fIuoride), PVDF, poled by a ramp voltage, and the poly(methyl metacrylate), PMMA, having a polar dye, poled with the carona triode. Measurements were performed far different poling conditions such as the maximum applied field and temperature
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2014-12-08
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
CeTI-SC/STI
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2021. Todos os direitos reservados.