Disertación de Maestría
DOI
10.11606/D.88.1995.tde-08062009-100248
Documento
Autor
Nombre completo
Luiz Henrique Dall'Antonia
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1995
Director
Tribunal
Tremiliosi Filho, Germano (Presidente)
D'Alkaine, Carlos Ventura
Ticianelli, Edson Antonio
Título en portugués
Caracterização eletroquímica e ótica de filmes de óxido espesso crescidos sobre ouro.
Palabras clave en portugués
Eletroquímica
Ouro
Óxidos espessos
Resumen en portugués
Através de polarização potenciostática de eletrodos de ouro policristalino em vários potenciais de polarização, 1,8,...., 2,4 V, ERH, por tempos de ate 72 h, em meios ácido e alcalino, conduz a formação de quatro estados do Óxido, OC1, OC2, OC3 e OC4, distinguíveis, durante o processo de redução pela técnica de voltametria cíclica. O estado quase-bidimensional (OC1) tende a um limite de duas monocamadas, em meio ácido, e penas uma em meio básico, de AuOads, enquanto, o filme espesso (OC2, OC3 e OC4, Au2O3) não atinge qualquer limite de crescimento. Os diagramas de carga catódica total (que mede o crescimento do filme de Óxido) vs log tempo de polarização revelam duas regiões lineares: (a) lenta, abaixa de 1 mC cm-2, (b) rápida, acima de 1 mC cm-2. Este comportamento é atribuído a um novo mecanismo de crescimento do óxido. Durante o crescimento do filme de óxido em altos potenciais anódicos, passando pelo vários estágios identificáveis por voltametria cíclica, pequenas mas significantes mudanças ocorrem na cinética de geração de O2. Os diagramas de Tafel revelam duas regiões lineares para a reação de geração de oxigênio, R.G.O., em meios ácido e alcalino. O mecanismo da R.G.O. é preliminarmente discutido. Finalmente, estudos dos filmes espesso de óxido de ouro foram realizados in situ por elipsometria espectroscópica. Os espectros do filme de óxido na faixa de comprimento de onda entre 300 e 800 nm, nos vários estágios de crescimento foram obtidos. Está mostrado que, ambos, a espessura do filme e o espectro ótico podem ser calculados em cada estágio durante o crescimento do óxido assumindo a existência de um filme fino altamente absorvente, adjacente à superfície do metal, e no topo deste um segundo filme que se assemelha mais a uma forma hidratada do "Au2O3". Este último filme atinge espessuras da ordem de várias centenas de A, quando polarizado por até 72 h.
Título en inglés
Eletrochemical and optical characterization of thick oxide films on gold electrodes.
Palabras clave en inglés
Eletrochemistry
Gold
Thick oxides
Resumen en inglés
Potentiostatic polarization of polycrystalline Au electrodes at various polarization potentials, 1.8, ..., 2.4 V, RHE, for polarization times up to 72h, in acid and basic solutions, leads to formation of four oxide states, OC1, OC2, OC3 and OC4, distinguished, in reduction, using linear-sweep voltammetry. The quasi-2d state (OC1) tends to the limit of two monolayers in acid solution and one monolayer in basic solution of AuOads, while the quasi-3d state (OC2-OC4, Au2O3) does not reach any limit in its extent. The cathodic total charge log polarization time plots reveal two linear regions: (a) slow, up to 1 mC cm-2, and (b) fast, beyond 1 mC cm-2. This behavior is attributed to a new oxide growth mechanism. During growth of the oxide film at high anodic potentials through the various stages identifiable in cyclic voltammetry, small but significant changes in the kinetics of O2, evolution arise. Tafel slopes for the oxygen evolution reaction, OER, reveal two linear region in acid and alkaline medium. The mechanism of the OER is preliminarily discussed. Finally, studies of the thick anodic oxide films on Au is done in situ by spectroscopic ellipsometry. The spectrum of the oxide film in the wavelength range 300 to 800 nm, at various stages of film growth is obtained. It is shown that both film thickness and optical spectrum can be solved at each stage in oxide growth assuming a highly absorbing thin film adjacent to the metal surface, and, on the top of it, a second film, which is most probably a hydrous form of "Au2O3". The latter film reaches thicknesses of severa1 hundreds A± up to 72h of anodization.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2009-06-15
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.