Mémoire de Maîtrise
DOI
10.11606/D.88.1995.tde-08062009-100248
Document
Auteur
Nom complet
Luiz Henrique Dall'Antonia
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 1995
Directeur
Jury
Tremiliosi Filho, Germano (Président)
D'Alkaine, Carlos Ventura
Ticianelli, Edson Antonio
Titre en portugais
Caracterização eletroquímica e ótica de filmes de óxido espesso crescidos sobre ouro.
Mots-clés en portugais
Eletroquímica
Ouro
Óxidos espessos
Resumé en portugais
Através de polarização potenciostática de eletrodos de ouro policristalino em vários potenciais de polarização, 1,8,...., 2,4 V, ERH, por tempos de ate 72 h, em meios ácido e alcalino, conduz a formação de quatro estados do Óxido, OC1, OC2, OC3 e OC4, distinguíveis, durante o processo de redução pela técnica de voltametria cíclica. O estado quase-bidimensional (OC1) tende a um limite de duas monocamadas, em meio ácido, e penas uma em meio básico, de AuOads, enquanto, o filme espesso (OC2, OC3 e OC4, Au2O3) não atinge qualquer limite de crescimento. Os diagramas de carga catódica total (que mede o crescimento do filme de Óxido) vs log tempo de polarização revelam duas regiões lineares: (a) lenta, abaixa de 1 mC cm-2, (b) rápida, acima de 1 mC cm-2. Este comportamento é atribuído a um novo mecanismo de crescimento do óxido. Durante o crescimento do filme de óxido em altos potenciais anódicos, passando pelo vários estágios identificáveis por voltametria cíclica, pequenas mas significantes mudanças ocorrem na cinética de geração de O2. Os diagramas de Tafel revelam duas regiões lineares para a reação de geração de oxigênio, R.G.O., em meios ácido e alcalino. O mecanismo da R.G.O. é preliminarmente discutido. Finalmente, estudos dos filmes espesso de óxido de ouro foram realizados in situ por elipsometria espectroscópica. Os espectros do filme de óxido na faixa de comprimento de onda entre 300 e 800 nm, nos vários estágios de crescimento foram obtidos. Está mostrado que, ambos, a espessura do filme e o espectro ótico podem ser calculados em cada estágio durante o crescimento do óxido assumindo a existência de um filme fino altamente absorvente, adjacente à superfície do metal, e no topo deste um segundo filme que se assemelha mais a uma forma hidratada do "Au2O3". Este último filme atinge espessuras da ordem de várias centenas de A, quando polarizado por até 72 h.
Titre en anglais
Eletrochemical and optical characterization of thick oxide films on gold electrodes.
Mots-clés en anglais
Eletrochemistry
Gold
Thick oxides
Resumé en anglais
Potentiostatic polarization of polycrystalline Au electrodes at various polarization potentials, 1.8, ..., 2.4 V, RHE, for polarization times up to 72h, in acid and basic solutions, leads to formation of four oxide states, OC1, OC2, OC3 and OC4, distinguished, in reduction, using linear-sweep voltammetry. The quasi-2d state (OC1) tends to the limit of two monolayers in acid solution and one monolayer in basic solution of AuOads, while the quasi-3d state (OC2-OC4, Au2O3) does not reach any limit in its extent. The cathodic total charge log polarization time plots reveal two linear regions: (a) slow, up to 1 mC cm-2, and (b) fast, beyond 1 mC cm-2. This behavior is attributed to a new oxide growth mechanism. During growth of the oxide film at high anodic potentials through the various stages identifiable in cyclic voltammetry, small but significant changes in the kinetics of O2, evolution arise. Tafel slopes for the oxygen evolution reaction, OER, reveal two linear region in acid and alkaline medium. The mechanism of the OER is preliminarily discussed. Finally, studies of the thick anodic oxide films on Au is done in situ by spectroscopic ellipsometry. The spectrum of the oxide film in the wavelength range 300 to 800 nm, at various stages of film growth is obtained. It is shown that both film thickness and optical spectrum can be solved at each stage in oxide growth assuming a highly absorbing thin film adjacent to the metal surface, and, on the top of it, a second film, which is most probably a hydrous form of "Au2O3". The latter film reaches thicknesses of severa1 hundreds A± up to 72h of anodization.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2009-06-15
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.