Mémoire de Maîtrise
DOI
10.11606/D.88.2007.tde-09042008-150513
Document
Auteur
Nom complet
Henrique Nogueira Soares
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 2007
Directeur
Jury
Tarpani, José Ricardo (Président)
Pereira, Luiz Edno
Spinelli, Dirceu
Titre en portugais
Detecção por raios-x de trincas de fadiga em juntas rebitadas de Glare®
Mots-clés en portugais
Fadiga
Junta rebitada
Laminado metal fibra
Material aeronáutico
Radiografia de raios-x
Resumé en portugais
Foi realizado um estudo comparativo da capacidade de duas variantes do método de radiografia por raios- X em detectar trincas de fadiga em juntas sobrepostas rebitadas de laminado híbrido metal-fibra Glare® de uso aeronáutico. Durante os ensaios mecânicos de fadiga sob amplitude constante de tensão, diversos corpos de prova rebitados foram periodicamente inspecionados por raios-X, em ambas as modalidades convencional e digital. Raios-X em filmes convencionais digital. Raios-X em filmes convencionais proporcionaram ótimo detalhamento de trincas nas juntas mecânicas, enquanto que as imagens geradas pela modalidade digital apresentaram qualidade muito inferior, prejudicando ou até mesmo impedindo a avaliação do grau de integridade estrutural das juntas rebitadas.
Titre en anglais
X-ray inspection of fatigue cracks in riveted lap joints of Glare&trade
Mots-clés en anglais
Airframe material
Fatigue
Ffiber metal-laminate
Riveted lap joint
X-ray radiography
Resumé en anglais
A comparison is performed on the ability of two modalities of nondestructive X-ray radiography method in detecting fatigue cracks in riveted lap joints of aeronautical grade fiber-metal laminate Glare™. During constant amplitude loading in fatigue testing riveted specimens were periodically inspected using both the conventional and digital X-ray methodology. Conventional film X-ray modality provided high quality images of growing cracks in the mechanical joints, whereas digital radiography generated faulty images, which impaired or even prevented the structural integrity assessment of the riveted joints.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
HenriqueSoares_M.pdf (20.93 Mbytes)
Date de Publication
2008-04-10
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.