Disertación de Maestría
DOI
10.11606/D.88.1998.tde-09122013-100919
Documento
Autor
Nombre completo
Nara Cristina de Souza
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1998
Director
Tribunal
Hernandes, Antonio Carlos (Presidente)
Machado, Walmir Guedes
Messaddeq, Younes
Título en portugués
Análise dos sistemas vítreos ternários Bi-Ge-B, Bi-Ge-Ga e um estudo de cristalização da fase Bi4Ge3O12
Palabras clave en portugués
Cristalização
Germanato de bismuto
Vidros óxidos
Resumen en portugués
Há um crescente interesse científico e tecnológico voltado para compostos cristalinos de óxido de bismuto com óxidos de germânio, silício ou titânio, por exibirem propriedades eletro e magnetoópticas, fotocondutivas e piezoelétricas. Sistemas vítreos com propriedades similares a estes compostos são de alto interesse, devido ao baixo custo e facilidade no procedimento de preparação em relação aos monocristais. Este trabalho teve como finalidade analisar o efeito de adição de óxidos de boro e gálio, ao sistema binário composto por óxido de bismuto com óxidos de germânio. A amostra vítrea de composição 45BiO1.5:40BO1.5:15GeO2 (BBG-8), apresentou alta reprodutibilidade e estabilidade térmica (ΔT=132, Hr=0.34 e S=26.74), sendo assim, selecionada para o estudo da cristalização. As fases cristalizadas nesta amostra, durante tratamento térmico, foram determinadas por análises de difração de raios-X e medidas composicionais. Foram cristalizadas as fases Bi6B10O24 e Bi4Ge3O12, sendo a última, a fase de interesse para nosso estudo. Métodos térmicos foram utilizados no estudo da cristalização da fase Bi4Ge3O12, possibilitando a verificação da energia de ativação (≈ 54Kcal/mol) pelos métodos de Ozawa e Chen, e a direcionalidade do crescimento dos cristais (nmédio=1.12). A fim de obtermos mais informações a respeito de cristalização utilizamos óptica eletrônica.
Título en inglés
Analysis of ternary glassy system Bi-Ge-B, Bi-Ge-Ga and a study of Bi4Ge3O12 phase crystallization
Palabras clave en inglés
Bismuth germanate
Crystallization
Oxide glasses
Resumen en inglés
The sillenite crystals, Bi12MO20 (M = Ge, Si, Ti), are interesting for applications such as optical memories, holography or optical phase conjugating devices. The eulytite crystals, Bi4M3O12, have been studied for their electro-optical, electromechanical and luminescence properties. These crystals am used as scintillators or, when doped with rare-earth elements, as laser materials. The study of glass systems, having properties similar to those crystals, is of high interest because of the lower cost and easier preparation procedures with respect to single crystals. The purpose of this work is the study of interaction of B2O3 and Ga2O3 with binary system Bi2O3-GeO2. The glassy sample BBG-8 (45BiO1.5:40BO1.5:15GeO2), was chosen far crystallition study, due to its high reproducibility and thermal stability. The presence of crystalline phases (Bi6B10O24 and Bi4Ge3O12), obtained after heat treatment, was investigated by powder X-ray diffraction and compositional analysis. The crystalline eulytite phase (Bi4Ge3O12) is an interest of our study. Thermal methods were used on the study of Bi4Ge3O12crystallization process of the sample BBG-8, and the value obtained, by means of Ozawa and Chen methods, was approximately 54Kcal/mol, and the directionality of crystal growth (n average) was equal to 1.12. To obtain further information on the crystallization mechanism we also performed microphotographic analysis.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2014-02-14
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.