Disertación de Maestría
DOI
10.11606/D.88.2010.tde-10032010-154039
Documento
Autor
Nombre completo
Sandra Tessutti Dias
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2010
Director
Tribunal
Li, Maximo Siu (Presidente)
Messaddeq, Younes
Zanatta, Antonio Ricardo
Título en portugués
Efeitos fotoinduzidos em vidros e filmes de fosfato de antimônio dopado com chumbo e fosfato de antimônio dopado com cromo
Palabras clave en portugués
Filmes finos
Fotoclareamento
Fotoexpansão
Luminescência
Vidros fosfato de antimônio
Resumen en portugués
O presente trabalho tem como objetivo estudar propriedades ópticas e estruturais de vidros e filmes de fosfato de antimônio dopados. Os vidros foram produzidos pela fusão a 900 °C, em cadinhos de carbono vítreo, dos precursores [Sb(PO3)3]n + Sb2O3 utilizando como dopantes o PbO e Cr2O3, sendo em seguida vertidos e resfriados rapidamente em moldes de aço inox. As composições vítreas em questão são: 20% [Sb(PO3)3]n 77% Sb2O3 3%PbO, 20 %[Sb(PO3)3]n 77% Sb2O3 3%Cr2O3 e 20 %[Sb(PO3)3]n 74% Sb2O3 6%Cr2O3 (mol%). A caracterização das amostras teve início com medidas de EDX para micro - análise composicional. Em seguida para os vidros na forma de bulk foram medidos os espectros de absorção e luminescência. As medidas de luminescência foram realizadas utilizando-se o laser de Kr+ nas linhas MLUV (350 nm) e MLVI (41 5nm). Medidas de EPR foram realizadas para os vidros dopados com Cr por estes possuírem elétrons desemparelhados. Os filmes finos foram depositados em substratos de soda lime pela técnica de evaporação de feixe de elétrons. A partir do espectro de absorção, o valor do bandgap (por volta de 3 eV) foi calculado, verificando que a melhor fonte para irradiação das amostras era o laser de Kr+ em MLUV. Apenas filmes de [Sb(PO3)3]n: 3% Pb2+ apresentaram efeito fotoestrutural. Com isso um estudo variando parâmetros, como tempo de irradiação, densidade de potência e espessura dos filmes, foi realizado a fim de observar a otimização do efeito. Acompanhado das variações fotoestruturais, ocorreram variações fotocrômicas, no caso fotoclareamento, as quais se caracterizaram por um deslocamento da borda de absorção para maiores energias, observado nos espectros de absorção das áreas irradiadas. Com os resultados observados do estudo e caracterização das amostras, algumas aplicações tecnológicas foram discutidas, como no caso dos efeitos observados nos filmes que podem ser utilizados para gravação de redes de difração.
Título en inglés
Photoinduced effects in glasses and films of lead doped antimony phosphate and chromium doped antimony phosphate
Palabras clave en inglés
Antimony phosphate glasses
Luminescence
Photobleaching
Photoexpansion
Thin films
Resumen en inglés
The present work is about the study of the optical and structure properties of doped antimony phosphate glasses and thin films. The glasses were produced by the melting of precursors [Sb(PO3)3]n + Sb2O3 using PbO and Cr2O3 as dopant at 900 °C in vitreous carbon crucibles, then poured and quickly cooled into steel molds. The vitreous composition are: 20% [Sb(PO3)3]n 77% Sb2O3 3%PbO, 20 %[Sb(PO3)3]n 77% Sb2O3 3%Cr2O3 e 20 %[Sb(PO3)3]n 74% Sb2O3 6%Cr2O3 (mol%). The samples characterization started with EDX measurements for compositional micro-analysis. Then for the glasses in bulks form the absorption and luminescence spectra were measured. The luminescence measurements were done using MLUV (350 nm) and MLVI (415 nm) of a Kr+ laser. EPR measurements were taken for the Cr doped glasses because they present unpaired electrons. The thin films were deposited on soda lime substrates by the electron beam evaporation technique. From absorption spectra, the bandgap value around 3 eV was evaluated, noting that the best irradiation source of the samples was using a MLUV of a Kr+ laser. Only [Sb(PO3)3]n: 3% Pb2+ films presented photostructural effects. Therefore a systematic study varying several parameters, like irradiation time, power density and film thickness was conducted to observe the effect optimization. Following the photostructural variation, occurred photocchromic effects, in this case, photobleaching effects, which were characterized by a displacement of absorption edge to lower energies, observed in the absorption spectra of the irradiated areas. With the observed results from the study and characterization of the samples, some technologies applications were discussed, like in the case of the observed films effects that can be used for recording diffraction gratings.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2010-03-19
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.