Master's Dissertation
DOI
10.11606/D.88.2017.tde-11072017-151910
Document
Author
Full name
Maximiliano dos Anjos Azambuja
Institute/School/College
Knowledge Area
Date of Defense
Published
São Carlos, 2002
Supervisor
Committee
Dias, Antonio Alves (President)
Jesus, José Manoel Henriques de
Sales, Almir
Title in Portuguese
Avaliação do adesivo poliuretano à base de mamona na fabricação de Madeira Laminada Colada (MLC)
Keywords in Portuguese
Adesivo de mamona
Madeira laminada colada
Madeira tratada
Parâmetros de colagem
Abstract in Portuguese
Este trabalho teve como finalidade o estudo da aplicação de um adesivo alternativo para a fabricação de madeira laminada colada (MLC). Este adesivo, à base de óleo de mamona, apresenta vantagens em relação ao tradicionalmente utilizado, considerando aspectos ecológicos e econômicos. Foram determinados parâmetros adequados para a colagem, e avaliada a compatibilidade entre adesivo e o tratamento com o preservativo hidrossolúvel de Arseniato de Cobre Cromatado (CCA - tipo C) e em madeiras sem o tratamento preservativo, em termos de resistência da linha da cola, por meio dos ensaios de cisalhamento, de tração normal e de tração paralela às fibras, usando a espécie Pinus caribea hondurensis. Com estes parâmetros, foram confeccionadas 12 vigas de MLC, utilizando-se as espécies de reflorestamento Pinus caribea hondurensis e Eucaliptus grandis. Foi avaliado o desempenho estrutural das vigas de MLC, por intermédio do ensaio mecânico de resistência à flexão, objetivando-se analisar a resistência da linha de cola. Os resultados obtidos permitem concluir o bom desempenho do adesivo poliuretano à base de mamona, para a aplicação em madeira não preservada e preservada com OCA tipo-C. A pressão de colagem indicada para laminação das vigas é 0,8% MPa para madeira não tratada, e 1,6 MPa para madeira tratada. Para a fabricação das emendas das lâminas recomenda-se a pressão de colagem igual a MPa, para madeira tratada ou não.
Title in English
Evaluation of the polyurethane adhesive base on castor oil to fabrication of glued laminated timber (GLULAM)
Keywords in English
Castor oil adhesive
Glued laminated timber
Gluing parameters
GLULAM
Abstract in English
The aim of this work is the study of the use of alternative adhesive for glued laminated timber (GLULAM). This adhesive, based on castor oil, presents ecological and economical advantages in relation of traditionally used. The appropriate parameters for gluing were determined and the compatibility between this adhesive and treatment with the waterbome preservative of chromated copper arsenate (CCA-C) were evaluated through shear tests and tensions tests (perpendicular and parallel to the grain), using the species Pinus caribea hondurensis. With these parameters, were made 12 beams of GLULAM; using the species Pinus caribea hondurensis and Eucaliptus grandis. The structural performance of the beams of GLULAM was evaluated through static bending tests. The results obtained allow concluding the good performance of the adhesive polyurethane based on castor oil, for use in wood not preserved and preserved with CCA type-C. The gluing pressures indicated are 0,8 MPa for non-treated wood, and 1,6 MPa for treated wood. The gluing pressure recommended for finger-joints is 9 MPa, for treated wood or not.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2017-07-12
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2019. All rights reserved.