Disertación de Maestría
DOI
10.11606/D.88.2017.tde-11072017-151910
Documento
Autor
Nombre completo
Maximiliano dos Anjos Azambuja
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2002
Director
Tribunal
Dias, Antonio Alves (Presidente)
Jesus, José Manoel Henriques de
Sales, Almir
Título en portugués
Avaliação do adesivo poliuretano à base de mamona na fabricação de Madeira Laminada Colada (MLC)
Palabras clave en portugués
Adesivo de mamona
Madeira laminada colada
Madeira tratada
Parâmetros de colagem
Resumen en portugués
Este trabalho teve como finalidade o estudo da aplicação de um adesivo alternativo para a fabricação de madeira laminada colada (MLC). Este adesivo, à base de óleo de mamona, apresenta vantagens em relação ao tradicionalmente utilizado, considerando aspectos ecológicos e econômicos. Foram determinados parâmetros adequados para a colagem, e avaliada a compatibilidade entre adesivo e o tratamento com o preservativo hidrossolúvel de Arseniato de Cobre Cromatado (CCA - tipo C) e em madeiras sem o tratamento preservativo, em termos de resistência da linha da cola, por meio dos ensaios de cisalhamento, de tração normal e de tração paralela às fibras, usando a espécie Pinus caribea hondurensis. Com estes parâmetros, foram confeccionadas 12 vigas de MLC, utilizando-se as espécies de reflorestamento Pinus caribea hondurensis e Eucaliptus grandis. Foi avaliado o desempenho estrutural das vigas de MLC, por intermédio do ensaio mecânico de resistência à flexão, objetivando-se analisar a resistência da linha de cola. Os resultados obtidos permitem concluir o bom desempenho do adesivo poliuretano à base de mamona, para a aplicação em madeira não preservada e preservada com OCA tipo-C. A pressão de colagem indicada para laminação das vigas é 0,8% MPa para madeira não tratada, e 1,6 MPa para madeira tratada. Para a fabricação das emendas das lâminas recomenda-se a pressão de colagem igual a MPa, para madeira tratada ou não.
Título en inglés
Evaluation of the polyurethane adhesive base on castor oil to fabrication of glued laminated timber (GLULAM)
Palabras clave en inglés
Castor oil adhesive
Glued laminated timber
Gluing parameters
GLULAM
Resumen en inglés
The aim of this work is the study of the use of alternative adhesive for glued laminated timber (GLULAM). This adhesive, based on castor oil, presents ecological and economical advantages in relation of traditionally used. The appropriate parameters for gluing were determined and the compatibility between this adhesive and treatment with the waterbome preservative of chromated copper arsenate (CCA-C) were evaluated through shear tests and tensions tests (perpendicular and parallel to the grain), using the species Pinus caribea hondurensis. With these parameters, were made 12 beams of GLULAM; using the species Pinus caribea hondurensis and Eucaliptus grandis. The structural performance of the beams of GLULAM was evaluated through static bending tests. The results obtained allow concluding the good performance of the adhesive polyurethane based on castor oil, for use in wood not preserved and preserved with CCA type-C. The gluing pressures indicated are 0,8 MPa for non-treated wood, and 1,6 MPa for treated wood. The gluing pressure recommended for finger-joints is 9 MPa, for treated wood or not.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2017-07-12
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.