Disertación de Maestría
DOI
https://doi.org/10.11606/D.88.2017.tde-11072017-165013
Documento
Autor
Nombre completo
Nestor Pedro Giacomini
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2003
Director
Tribunal
Leão, Alcides Lopes (Presidente)
Agnelli, José Augusto Marcondes
Frollini, Elisabete
Título en portugués
Compósitos reforçados com fibras naturais para a indústria automobilística
Palabras clave en portugués
Compósitos
Curauá
Fibras naturais
Indústria automotiva
Prensagem a frio
Sisal
Resumen en portugués
Este trabalho tem como finalidade o desenvolvimento de compósitos a base de resina de poliéster insaturado reforçados com fibras naturais visando aplicações na indústria automotiva. Foram obtidas amostras em escala semi-industrial de compósitos reforçados com fibra de curauá, sisal e vidro, com teores variando de 15 a 40% em massa, com e sem a adição de carga mineral na matriz polimérica, através do processo de prensagem a frio. Os efeitos de cada um dos fatores foram analisados sobre a resistência à tração, módulo de elasticidade, alongamento na ruptura, resistência à flexão e ao impacto. Além disso, foi determinado o comportamento dos materiais com diferentes composições com relação à absorção de umidade. A variação da resistência à flexão como função do tempo de imersão e do teor de umidade absorvido pelos diferentes materiais foi determinada. Foram analisadas as propriedades superficiais como brilho, neblina (haze), ondulância (long-waviness) para as amostras produzidas e submetidas a ensaios de envelhecimento térmico, câmara de condensação e envelhecimento artificial. Todos os resultados obtidos foram baseados em normas da indústria automobilística para verificar conformidade com as exigências do setor.
Título en inglés
Natural fiber reinforced composites for automotive applications
Palabras clave en inglés
Automotive industry
Composites
Natural fibers
Resumen en inglés
The purpose of this work is to develop unsaturated polyester based composites reinforced with natural fibers of automotive applications. Samples have been obtained in a semi-industrial scale of composites reinforced with curauá, sisal and glass fiber, with contents varying from 15 to 40% in weight, with and without mineral filler incorporation to the polyester matrix. The molding technique employed was compression molding. The effects of these variables have been investigated over the tensile strenght, young's modulus, strain at rupture, flexural and impact strenght of the materials. The behavior of each sample has been investigated concerning water absorption. The variation of flexural strenght as a function of water absorption and immersion time has been determined for each formulation studied. Surface properties such as gloss, haze, long and short-waviness have been determined for all samples obtained just after painting and after artificial weathering, thermal aging and water absorption tests. All results have been performed based on automotive standards in order to evaluate the conformance of the materials to the requirements of the industry.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2017-07-12
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.