Tese de Doutorado
DOI
10.11606/T.88.2004.tde-11092007-104457
Documento
Autor
Nome completo
Gilmara de Oliveira Machado
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Carlos, 2004
Orientador
Banca examinadora
Pawlicka, Agnieszka Joanna (Presidente)
Gonzalez, Jose Pedro Donoso
Kawano, Yoshio
Oliveira Junior, Osvaldo Novais de
Torresi, Roberto Manuel
Título em português
Preparação e caracterização de eletrólitos sólidos poliméricos a partir dos derivados de celulose - hidroxietilcelulose e hidroxipropilcelulose
Palavras-chave em português
Derivados de celulose
Eletrólitos sólidos poliméricos
Plastificação da HEC
Reação de entrecuzamento da HPC
Resumo em português
Esta tese apresenta os resultados da obtenção de eletrólitos sólidos poliméricos a partir dos derivados de celulose - hidroxipropilcelulose (HPC) e hidroxietilcelulose (HEC), ambas comerciais. Para atingir os objetivos do projeto, os dois derivados passaram por diferentes processos sendo que a HEC foi modificada fisicamente por meio de plastificação com glicerol e HPC foi alterada quimicamente. A transformação química consistiu nas reações de oxidação de grupos hidroxila da HPC em grupos cetona que, em seguida, foram submetidos as reações de enxertia com diamina de poli(óxido de propileno) [Jeffamina] resultando em redes por meio de ligações imina. A adição do sal perclorato de lítio, em diferentes concentrações, na matriz plastificada ou entrecruzada, resultou na obtenção de eletrólitos sólidos poliméricos, todos na forma de filmes. A caracterização destes eletrólitos foi realizada com técnicas básicas de caracterização de materiais como: análises térmicas (DSC, TGA), análise térmica dinâmico-mecânica (DMTA), análises estruturais (raios-X), medidas espectroscópicas (IR, UVNIS), análise elementar, microscopia eletrônica de varredura (SEM), e, como a mais importante, medidas de condutividade iônica utilizando a técnica de espectroscopia de impedância eletroquímica (EIS).
Título em inglês
Preparation and characterization of solid polymeric electrolytes based on hydroxypropylcellulose and hydroxyethlcellulose
Palavras-chave em inglês
Cellulose derivatives
Networks of HPC
Plasticization process
Solid polymeric electrolyte
Resumo em inglês
The present thesis reports the preparation and characterization of new types of solid polymeric electrolytes (SPE) based on cellulose derivatives such as hydroxypropylcellulose (HPC) and hydroxyethylcellulose (HEC), both commercial products. Aiming to reach this purpose both derivatives were subjected to modification processes, where HEC were physically modified by plasticization process with glycerol and HPC were submitted to chemical reactions. The latter ones were promoted by the oxidation of HPC hydroxyl groups and ketone groups and then subjected to grafting with diamine poly(propylene oxide) (Jeffamine), resulting in the imine bond network formation. Different concentrations of lithium salt were added to the plasticized and grafted samples, resulting in solid polymeric electrolytes, all in the film form. The characterization of these samples was performed by thermal analysis (DSC, TGA and DMTA), X-ray diffraction (XDR), scanning electron microscopy (SEM), ultraviolet/visible/near-infrared spectroscopy (UV/Vis/NIR) and, as most important, measured of ionic conductivity using the technique of electrochemical impedance spectroscopy (EIS).
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
GilmaraMachado.pdf (6.35 Mbytes)
Data de Publicação
2007-09-12
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2021. Todos os direitos reservados.