Disertación de Maestría
DOI
10.11606/D.88.2016.tde-14092016-120013
Documento
Autor
Nombre completo
Marcus Alberto Della Coletta
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2000
Director
Tribunal
Casteletti, Luiz Carlos (Presidente)
Bolfarini, Claudemiro
Ishikawa, Tomaz Toshimi
Título en portugués
Comparação do desempenho à abrasão dos aços AISI 4340, 4140, 5140 e 300M nitretados por plasma em diferentes condições
Palabras clave en portugués
Aços
Nitretação
Nitretação iônica
Plasma
Resumen en portugués
Os aços de ultra resistência com médio carbono e baixa liga apresentam excelentes propriedades de resistência mecânica e à fadiga além de uma elevada temperabilidade. No entanto, tais aços apresentam o fenômeno da têmpera ou de tratamentos superficiais. O aço 300M foi desenvolvido visando a ampliação desta faixa, permitindo tratamentos em temperaturas em torno de 350ºC viabilizando o emprego da técnica de nitretação do mesmo por plasma sem a consequente fragilização. Neste trabalho comparou-se as características e propriedades do aço 300M nitretado por plasma à 350ºC e 550ºC com os aços de alta-resistência AISI 4340, 4140 e 5140 nitretados à 550ºC. Variou-se as condições de tratamento de forma a verificar a influência do tempo de nitretação e de frequência de pulso nas camadas nitretadas. Verificou-se que a nitretação por plasma demostrou ser bastante efetiva para conferir resistência ao desgaste abrasivo para todos os aços nitretados. O aço 300M nitretado em 350ºC apresentou no ensaio de desgaste abrasivo comportamento similar aos demais aços nitretados em 550ºC, enquanto que o melhor resultado geral foi alcançado pelo 300M nitretado à 550ºC em CC durante 6 horas, devido à formação de uma camada dupla de levada dureza e espessura.
Título en inglés
Comparison of performance of AISI 4340, 4140, 5140 and 300M steels nitrited by plasma in different conditions
Palabras clave en inglés
Ion nitriding
Nitriding
Plasma
Steels
Resumen en inglés
The ultrahigh-strength steels with medium carbon and low alloy, like AISI 4340, show excellent tensile strength and fatigue properties further higher hardenability. However, these steels have the phenomenon of tempering embrittlement, that restrict the temperature of treatments after quench or surfaces treatments. The 300M steel was developed aiming the enlargement this area of application, this steel permits treatments in temperatures about 350°C what allowed to use the plasma nitriding without problems with the embrittlement. In this production were compared the properties of the nitrited layers of the 300M nitriding by plasma in 350°C and 550°C with the steels AISI 4340, AISI 4140, AISI 5140 nitriding in 550°C. Plasma nitriding conditions like time and pulse frequency were varied. It was checked that the plasma nitriding showed good performance to improve the resistance to the abrasive wear in ali the steels tested. The 300M steel nitrited in 350°C showed results similar to the others in the pin-on-disk test and the better result occurred to the 300M steel nitrited in 550°C in dC plasma during 6 hours, because of a duble compound lawyer that arouse with a high thickness and high hardness.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2016-09-14
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.