Disertación de Maestría
DOI
10.11606/D.88.2016.tde-14092016-124243
Documento
Autor
Nombre completo
Cloir Salatiel da Silva
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1999
Director
Tribunal
Rollo, João Manuel Domingos de Almeida (Presidente)
Freire, Célia Marina de Alvarenga
Malite, Maximiliano
Título en portugués
Análise microestrutural em altas temperaturas de um ferro fundido branco de alto cromo com molibdênio e nióbio
Palabras clave en portugués
Curva TTT
Dilatometria
Ferro fundido branco de alto cromo
Metalografia em altas temperaturas
Microscopia eletrônica de varredura
Molibdênio
Nióbio
Resumen en portugués
As mudanças microestruturais, causadas pela adição de elementos de liga e pelos tratamentos térmicos, modificam as propriedades mecânicas e tribológicas dos materiais. Foi desenvolvido então um estudo em amostras de um ferro fundido branco de alto cromo com molidbênio e nióbio, procurando determinar os efeitos dos elementos de liga molibdênio e nióbio, na microestrutura deste material, através de medidas de dureza, dilatometria, ataque químico, microscopia eletrônica de varredura e,principalmente, a utilização de metalografia em altas temperaturas. A técnica de metalografia em altas temperaturas permite o estudo das mudanças microestruturais durante os ciclos térmicos, que foram programados, tendo como referência a curva TTT previamente traçada para este material, focalizando regiões onde não ocorrem mudanças de fase. Deste modo foram obtidas as aparências metalográficas em altas temperaturas e feito um estudo comparativo com as outras técnicas usadas. Com isto é possível melhorar o conhecimento sobre a microestrutura do material em questão e obter ligas com propriedades pré-determinadas.
Título en inglés
A molybdenum and niobium high chromium white cast iron study-metallography at high temperatures
Palabras clave en inglés
Dilatometry
High temperature metallography
Molybdenum
Niobium
Scanning electron microscopy
TTT curve
White cast iron of high chromium
Resumen en inglés
The microstructural changes caused by the addition of alloying elements and by thermal treatments modify the mechanical and tribological properties of the materials. A study was develop on samples of molybdenum and niobium high chromium white cast iron, trying to determine the effects of molybdenum and niobium alloys elements on microstructure of this material through hardness measurements, dilatometry, chemical etching, scanning electron microscopy, and mainly, utilizing metallography at high temperatures. The metallography at high temperatures technic allows the study of microstructural changes during the thermal cyc1es, which were scheduled, having as reference the TTT curve previously traced to this material, focusing regions where changes of fase don't occur. So the metallographic appearances at high temperatures were obtained and it was done a comparative study using other technics. Because of that is possible to improve the knowledge of the material microstructure, which it has been studied, and to obtain alloys with predetermined properties.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2016-09-14
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.