Mémoire de Maîtrise
DOI
10.11606/D.88.2016.tde-14092016-124243
Document
Auteur
Nom complet
Cloir Salatiel da Silva
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 1999
Directeur
Jury
Rollo, João Manuel Domingos de Almeida (Président)
Freire, Célia Marina de Alvarenga
Malite, Maximiliano
Titre en portugais
Análise microestrutural em altas temperaturas de um ferro fundido branco de alto cromo com molibdênio e nióbio
Mots-clés en portugais
Curva TTT
Dilatometria
Ferro fundido branco de alto cromo
Metalografia em altas temperaturas
Microscopia eletrônica de varredura
Molibdênio
Nióbio
Resumé en portugais
As mudanças microestruturais, causadas pela adição de elementos de liga e pelos tratamentos térmicos, modificam as propriedades mecânicas e tribológicas dos materiais. Foi desenvolvido então um estudo em amostras de um ferro fundido branco de alto cromo com molidbênio e nióbio, procurando determinar os efeitos dos elementos de liga molibdênio e nióbio, na microestrutura deste material, através de medidas de dureza, dilatometria, ataque químico, microscopia eletrônica de varredura e,principalmente, a utilização de metalografia em altas temperaturas. A técnica de metalografia em altas temperaturas permite o estudo das mudanças microestruturais durante os ciclos térmicos, que foram programados, tendo como referência a curva TTT previamente traçada para este material, focalizando regiões onde não ocorrem mudanças de fase. Deste modo foram obtidas as aparências metalográficas em altas temperaturas e feito um estudo comparativo com as outras técnicas usadas. Com isto é possível melhorar o conhecimento sobre a microestrutura do material em questão e obter ligas com propriedades pré-determinadas.
Titre en anglais
A molybdenum and niobium high chromium white cast iron study-metallography at high temperatures
Mots-clés en anglais
Dilatometry
High temperature metallography
Molybdenum
Niobium
Scanning electron microscopy
TTT curve
White cast iron of high chromium
Resumé en anglais
The microstructural changes caused by the addition of alloying elements and by thermal treatments modify the mechanical and tribological properties of the materials. A study was develop on samples of molybdenum and niobium high chromium white cast iron, trying to determine the effects of molybdenum and niobium alloys elements on microstructure of this material through hardness measurements, dilatometry, chemical etching, scanning electron microscopy, and mainly, utilizing metallography at high temperatures. The metallography at high temperatures technic allows the study of microstructural changes during the thermal cyc1es, which were scheduled, having as reference the TTT curve previously traced to this material, focusing regions where changes of fase don't occur. So the metallographic appearances at high temperatures were obtained and it was done a comparative study using other technics. Because of that is possible to improve the knowledge of the material microstructure, which it has been studied, and to obtain alloys with predetermined properties.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2016-09-14
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.