Dissertação de Mestrado
DOI
10.11606/D.88.2016.tde-14092016-124243
Documento
Autor
Nome completo
Cloir Salatiel da Silva
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Carlos, 1999
Orientador
Banca examinadora
Rollo, João Manuel Domingos de Almeida (Presidente)
Freire, Célia Marina de Alvarenga
Malite, Maximiliano
Título em português
Análise microestrutural em altas temperaturas de um ferro fundido branco de alto cromo com molibdênio e nióbio
Palavras-chave em português
Curva TTT
Dilatometria
Ferro fundido branco de alto cromo
Metalografia em altas temperaturas
Microscopia eletrônica de varredura
Molibdênio
Nióbio
Resumo em português
As mudanças microestruturais, causadas pela adição de elementos de liga e pelos tratamentos térmicos, modificam as propriedades mecânicas e tribológicas dos materiais. Foi desenvolvido então um estudo em amostras de um ferro fundido branco de alto cromo com molidbênio e nióbio, procurando determinar os efeitos dos elementos de liga molibdênio e nióbio, na microestrutura deste material, através de medidas de dureza, dilatometria, ataque químico, microscopia eletrônica de varredura e,principalmente, a utilização de metalografia em altas temperaturas. A técnica de metalografia em altas temperaturas permite o estudo das mudanças microestruturais durante os ciclos térmicos, que foram programados, tendo como referência a curva TTT previamente traçada para este material, focalizando regiões onde não ocorrem mudanças de fase. Deste modo foram obtidas as aparências metalográficas em altas temperaturas e feito um estudo comparativo com as outras técnicas usadas. Com isto é possível melhorar o conhecimento sobre a microestrutura do material em questão e obter ligas com propriedades pré-determinadas.
Título em inglês
A molybdenum and niobium high chromium white cast iron study-metallography at high temperatures
Palavras-chave em inglês
Dilatometry
High temperature metallography
Molybdenum
Niobium
Scanning electron microscopy
TTT curve
White cast iron of high chromium
Resumo em inglês
The microstructural changes caused by the addition of alloying elements and by thermal treatments modify the mechanical and tribological properties of the materials. A study was develop on samples of molybdenum and niobium high chromium white cast iron, trying to determine the effects of molybdenum and niobium alloys elements on microstructure of this material through hardness measurements, dilatometry, chemical etching, scanning electron microscopy, and mainly, utilizing metallography at high temperatures. The metallography at high temperatures technic allows the study of microstructural changes during the thermal cyc1es, which were scheduled, having as reference the TTT curve previously traced to this material, focusing regions where changes of fase don't occur. So the metallographic appearances at high temperatures were obtained and it was done a comparative study using other technics. Because of that is possible to improve the knowledge of the material microstructure, which it has been studied, and to obtain alloys with predetermined properties.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2016-09-14
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
CeTI-SC/STI
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2019. Todos os direitos reservados.