Mémoire de Maîtrise
DOI
10.11606/D.88.2002.tde-14112014-102419
Document
Auteur
Nom complet
Flávia Maria Marconi
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 2002
Directeur
Jury
Balogh, Debora Terezia (Président)
Bonagamba, Tito Jose
Viertler, Hans
Titre en portugais
Síntese e caracterização de polímeros com propriedades eletroluminescentes
Mots-clés en portugais
Eletroluminescência
LEDs
Poli (p-fenileno-vinileno)
PPV
Síntese
Resumé en portugais
Durante este trabalho foram sintetizados e caracterizados três derivados dialcoxilados do poli(p-fenileno-vinileno) que diferem entre si pelo tamanho de uma das cadeias laterais: o poli(2-metoxi-5-hexiloxi-p-fenileno-vinileno), MH-PPV, o poli(2-metoxi-5-dodecoxi-p-fenileno-vinileno), MD-PPV e o poli(2-metoxi-5-hexadecoxi- p-fenileno-vinileno), MHd-PPV. Esses polímeros apresentam propriedades eletroluminescentes e podem ser utilizados em dispositivos emissores de luz. A síntese consiste de três etapas: síntese do éter aromático; bisclorometilação do éter aromático, gerando o monômero; e polimerização. A maior diferença no processo de síntese foi observada na obtenção do monômero, sendo necessário um maior excesso de reagente e maiores tempos de reação para a obtenção do monômero do MD-PPV e do MHd-PPV do que para o MH-PPV. Todos os produtos foram caracterizados principalmente por espectroscopia na região do infravermelho, FTIR, e por Ressonância Magnética Nuclear de próton e carbono 13. A estrutura química dos polímeros foi confirmada por FTIR e as massas moleculares foram determinadas por Cromatografia de Exclusão por Tamanho, revelando uma alta polidispersividade e valores de massa molecular ponderal média (Mw) da ordem de 105. A análise térmica revelou valores de temperatura de transição vítrea, Tg e amolecimento, Ts, acima de 100oC, e ainda temperaturas de decomposição acima de 400oC para os três polímeros. O MHd-PPV, apresentou, além da Tg, uma transição em tomo de 50oC que pode estar relacionada à fusão das cadeias laterais. Filmes dos três polímeros preparados a partir de diferentes solventes apresentaram diferentes morfologias, observadas por Microscopia de Força Atômica, posições de máxima absorção (500-520 nm) e emissão (585-600 nrn) com pequenas variações e processos de fotodegradação com diferentes características, em função do solvente utilizado. Assim, as diferentes cadeias laterais apresentaram efeitos principalmente sobre características como temperatura de transição vítrea e morfologia dos filmes poliméricos, e, em consequência desta última, sobre o formato dos espectros de emissão e sobre o processo de degradação
Titre en anglais
Synthesis and characterization of polymers with electroluminescent properties
Mots-clés en anglais
Electroluminescence
LEDs
poly(p-phenylene-vinylene)
PPV
Synthesis
Resumé en anglais
In this work, three dialkoxy derivatives of poly(p-phenylenevinylene),which differs from each other by the size of the side chain, were synthesized and characterized: the poly(2-methoxy-5-hexyloxy-p-phenylenevinylene), MH-PPV, the poly(2-methoxy-5-dodecoxy-p-phenylene-vinylene), MD-PPV and the poly(2-methoxy- 5-hexadecoxi-p-phenylene-vinyleno), MHd-PPV. These polymers have electroluminescent properties and can be used in light emitting devices. The synthesis consists in three steps: synthesis of aromatic ether, bischloromethylation of the ether yielding the monomer, and polymerization. The major difference regarding the synthesis processes lies on the monomer synthesis. A larger excess of reagents and longer reaction times were necessary to obtain the MD-PPV and MHd-PPV than that used to obtain the MH-PPV. All the products of the two first steps were characterized mainly by FTIR and NMR (proton and carbon 13). The chemical structures of the polymers were confirmed by FTIR and the molar masses determined by characterized by Size Exclusion Chromatography, revealing a high polydispersity and values of mean mass molecular weight (Mw) around 105. The thermal analysis presented values of glass transition temperatures, Tg, and softening, Ts, above 100 oC, and decomposition temperatures above 400oC for the three polymers. The MHd-PPV, presented, besides the Tg, a transition in 50oC, which may be related to the melting of the side chain. Films of the three polymers prepared from different solvents presented different morphologies, as observed by Atomic Force Microsocopy, slightly different absorptions (500-520 nm) and emission (585-600 nm) maxima and different photo-degradation processes depending on the solvent used to prepare the films. Therefore, the different size of the side chain presented effects mainly on characteristics as thermal transitions and film morphologies, and, in consequence of the late, on the shape of the emission and on the degradation properties
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2014-11-21
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.