Master's Dissertation
DOI
10.11606/D.88.2017.tde-14112017-155843
Document
Author
Full name
Marcia Fernanda Martins Dias
Institute/School/College
Knowledge Area
Date of Defense
Published
São Carlos, 1997
Supervisor
Committee
Gomes, Samuel Irati Novaes (President)
Bose Filho, Waldek Wladimir
Kobayashi, Yukio
Title in Portuguese
Efeito dos consumíveis no metal depositado com e sem adição de pó metálico em aço de resistência ambiental
Keywords in Portuguese
Aço de resistência ambiental
Adição de pó metálico
Austenita retida
Metal de solda
Propriedades mecânicas
Abstract in Portuguese
Neste trabalho foi feito o estudo comparativo da composição química, da microestrutura e das propriedades mecânicas entre metais de solda com e sem adição de pó metálico de aço alta resistência baixa liga (ARBL). Foram feitos oito cordões pelo processo de soldagem por arco submerso, utilizando-se corrente de 660A, tensão de 34V, velocidade de soldagem de 28,8 cm/min e vazão de pó de 4,5 kg/h. Foram utilizados os arames EM-12K e EB-2, os fluxos OK1071 e BX200. O arame e o fluxo foram alternados para os oito cordões de solda. Foi adicionado o pó metálico PD-3 em quatro cordões de solda. Utilizou-se chapa de aço USI-SAC-50. Fez-se a metalografia, a quantificação da microestrutura e da austenita retida dos oito cordões. Os cordões sem adição de pó metálico apresentaram maiores porcentagens de ferrita acicular e maiores porcentagens de austenita retida. As propriedades mecânicas foram obtidas por ensaios de dureza, tração e impacto. Os cordões sem adição de pó apresentaram maiores valores de dureza e maiores limites de escoamento. Dos resultados obtidos foi concluído que a austenita retida influenciou na queda do patamar de energia dúctil para metais de solda com baixos teores de oxigênio e também influenciou no aumento da AFTI (aparência da fratura na temperatura de transição) quando em porcentagens relativamente altas nos cordões de solda como soldados.
Title in English
not available
Keywords in English
not available
Abstract in English
The comparative study of the composition, microstructure and mechanical properties among weld metals with and without alloyed metal powder of High Strength Low Alloyed (HSLA) steel were dane. Eight submerged are weld metals were made, using welding current of 660A, are voltage of 34V, travel speed of 28,8 cm/min and a powder flow of 4,5 kg/h. EM-12K and EB-2 wires and OK1071 and BX200 fluxes were used. The wire and the flux were alternated for eight weld metals. PD-3 alloyed metal powder was used in four weld metals. The USI/SAC-50 steel was used in this work. The metallography, microstructure quantification and retained austenite quantification of eight weld metals were done. The weld metals without alloyed metal powder showed higher percentages of acicular ferrite and retained austenite. The mechanical properties were obtained through tests of hardness, strength and impact. The weld metals without alloyed metal powder showed higher hardness and yield strength. From the results obtained, it was concluded that the retained austenite influenced on both depress of the upper shelf depressed for weld metals with low oxygen content and on the increase of the fracture appearance transition temperature (FATT), when in higher percentages, in weld metals as-welded.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2017-11-14
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2019. All rights reserved.