Disertación de Maestría
DOI
10.11606/D.88.2017.tde-14112017-155843
Documento
Autor
Nombre completo
Marcia Fernanda Martins Dias
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1997
Director
Tribunal
Gomes, Samuel Irati Novaes (Presidente)
Bose Filho, Waldek Wladimir
Kobayashi, Yukio
Título en portugués
Efeito dos consumíveis no metal depositado com e sem adição de pó metálico em aço de resistência ambiental
Palabras clave en portugués
Aço de resistência ambiental
Adição de pó metálico
Austenita retida
Metal de solda
Propriedades mecânicas
Resumen en portugués
Neste trabalho foi feito o estudo comparativo da composição química, da microestrutura e das propriedades mecânicas entre metais de solda com e sem adição de pó metálico de aço alta resistência baixa liga (ARBL). Foram feitos oito cordões pelo processo de soldagem por arco submerso, utilizando-se corrente de 660A, tensão de 34V, velocidade de soldagem de 28,8 cm/min e vazão de pó de 4,5 kg/h. Foram utilizados os arames EM-12K e EB-2, os fluxos OK1071 e BX200. O arame e o fluxo foram alternados para os oito cordões de solda. Foi adicionado o pó metálico PD-3 em quatro cordões de solda. Utilizou-se chapa de aço USI-SAC-50. Fez-se a metalografia, a quantificação da microestrutura e da austenita retida dos oito cordões. Os cordões sem adição de pó metálico apresentaram maiores porcentagens de ferrita acicular e maiores porcentagens de austenita retida. As propriedades mecânicas foram obtidas por ensaios de dureza, tração e impacto. Os cordões sem adição de pó apresentaram maiores valores de dureza e maiores limites de escoamento. Dos resultados obtidos foi concluído que a austenita retida influenciou na queda do patamar de energia dúctil para metais de solda com baixos teores de oxigênio e também influenciou no aumento da AFTI (aparência da fratura na temperatura de transição) quando em porcentagens relativamente altas nos cordões de solda como soldados.
Título en inglés
not available
Palabras clave en inglés
not available
Resumen en inglés
The comparative study of the composition, microstructure and mechanical properties among weld metals with and without alloyed metal powder of High Strength Low Alloyed (HSLA) steel were dane. Eight submerged are weld metals were made, using welding current of 660A, are voltage of 34V, travel speed of 28,8 cm/min and a powder flow of 4,5 kg/h. EM-12K and EB-2 wires and OK1071 and BX200 fluxes were used. The wire and the flux were alternated for eight weld metals. PD-3 alloyed metal powder was used in four weld metals. The USI/SAC-50 steel was used in this work. The metallography, microstructure quantification and retained austenite quantification of eight weld metals were done. The weld metals without alloyed metal powder showed higher percentages of acicular ferrite and retained austenite. The mechanical properties were obtained through tests of hardness, strength and impact. The weld metals without alloyed metal powder showed higher hardness and yield strength. From the results obtained, it was concluded that the retained austenite influenced on both depress of the upper shelf depressed for weld metals with low oxygen content and on the increase of the fracture appearance transition temperature (FATT), when in higher percentages, in weld metals as-welded.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2017-11-14
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.