Disertación de Maestría
DOI
10.11606/D.88.2004.tde-15092014-173003
Documento
Autor
Nombre completo
Juliana Maria de Albuquerque Gimenez
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2004
Director
Tribunal
Grandini, Carlos Roberto (Presidente)
Florêncio, Odila
Hernandes, Antonio Carlos
Título en portugués
Estudo da mobilidade de oxigênio intersticial em Bi2Sr2CaCu2O8+δ através de espectroscopia anelástica
Palabras clave en portugués
Atrito interno
Mobilidade de oxigênio intersticial
Supercondutividade
Resumen en portugués
Desde a descoberta dos supercondutores com alta temperatura crítica, muitos estudos têm sido realizados em tomo de suas propriedades fisicas, tentando associá-Ias à supercondutividade. Átomos de oxigênio dissolvidos intersticialmente têm um papel importante na supercondutividade destes materiais, pois são capazes de mover-se com facilidade dentro da rede além de contribuírem na criação de buracos nos planos de CUO2. As medidas de atrito interno são ferramentas sensíveis ao estudo de defeitos em sólidos, em particular a mobilidade de oxigênio intersticial. Neste trabalho, foram analisadas amostras de Bi2Sr2CaCu2O8+δ da maneira como foram recebidas, recozidas e dopadas com diferentes concentrações de oxigênio não estequiométrico. Foram efetuadas medidas de espectroscopia anelástica utilizando um pêndulo de torção invertido tipo Kê, operando com freqüência de oscilação de 11 a 30 Hz, num intervalo de temperatura compreendido entre 88 e 700 K, com taxa de aquecimento de 1 K/min e vácuo em tomo de 10-5 Torr. Foram observadas estruturas de relaxação complexas para as amostras recozidas, que são reversíveis apenas com novos tratamentos de recozimento, atribuídas a possíveis transições de fase estruturais. Para as amostras dopadas com oxigênio, foram observadas estruturas de relaxação que foram atribuídas ao movimento de átomos intersticiais de oxigênio nos planos de BiO. Foi observada também uma relação entre a intensidade dos processos de relaxação e a concentração dos intersticiais presentes nestas amostras.
Título en inglés
Study of oxygen interstitial mobility in Bi2Sr2CaCu2O8+δ by anelastic spectroscopy measurements
Palabras clave en inglés
Internal friction
Mobility of interstitial oxygen
Superconductivity
Resumen en inglés
Since the discovery of the high critical temperature superconductors many studies have been carried out intending to associate their physical properties to the superconductivity mechanisms. The oxygen atoms interstitially dissolved in its structure have an important role in the superconductivity of these materiaIs since they have high mobility capable to move through the net contributing to the generation of holes along the CUO2 plans. The internal friction measurements are a sensitive tool to the study of defects in solids, in particular the mobility of interstitial oxygen. In this work, it had been analyzed samples of Bi2Sr2CaCu2O8+δ in the as received condition, annealed and doped with different concentrations of not stoichiometric oxygen. The anelastic spectroscopy measurements were made using a torsional inverted pendulum of the Kê type, operating with oscillation frequency between 11 and 30 Hz, the applied temperatures are in the range between 88 and 700 K, with heating rate about 1 K/min and vacuum better than 10-5 Torr. Complex structures of relaxation had been observed for the annealed samples, they are reversible only with new annealing treatments. These structures were attributed to possible structural phase transitions. For the oxygen doped samples, the relaxation structures had been attributed to the mobility of interstitial oxygen atoms in the plans of BiO. On these measurements was also observed a relation between the intensity of the relaxation processes and the concentration ofthe interstitial oxygen in these samples.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2014-10-09
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.