Doctoral Thesis
DOI
10.11606/T.88.2016.tde-15092016-122338
Document
Author
Full name
Gil Eduardo Guimarães
Institute/School/College
Knowledge Area
Date of Defense
Published
São Carlos, 1999
Supervisor
Committee
Gomes, Samuel Irati Novaes (President)
Canale, Lauralice de Campos Franceschini
Ferreira, Itamar
Ishikawa, Tomaz Toshimi
Spinelli, Dirceu
Title in Portuguese
Avaliação microestrutural e das propriedades mecânicas de aço ARBL de resistência ambiental soldado a arco submerso com adição de pó metálico
Keywords in Portuguese
Adição de pó metálico
Soldagem arco submerso
Abstract in Portuguese
Estudos anteriores mostraram que a soldagem de aço USI-SAC-50 com adição de pó metálico pode promover o aparecimento de microfases que interferem nas propriedades mecânicas. Este trabalho, teve o objetivo de estudar os efeitos de variações nos consumíveis, aporte de calor e do tratamento térmico pós-soldagem na diminuição ou eliminação das microfases. Chapas de aço USI-SAC-50 foram soldadas por arco submerso com adição de pó metálico utilizando-se fluxos de soldagem BX-200 e OK-1071,arames de soldagem EM-12K e EB-2 e aportes de calor de 4,8 kJ/mm e 3,6 kJ/mm. Tensão e corrente foram mantidas em 34 V e 600 A, respectivamente. Após a soldagem, metade das chapas foi submetida a um tratamento térmico de alívio de tensões a 580ºC por 1 h. Foram realizados ensaios mecânicos de dureza, tração a -10ºC e CTOD a -10ºC, assim como foram realizadas metalografias preto e branco e coloridas para identificação e quantificação de fases. As composições químicas obtidas nos cordões de solda foram adequadas para que a quantidade de ferrita acicular presente assegurasse as boas propriedades mecânicas. As mudanças na composição química, em relação à trabalhos anteriores, ocasionadas pela variação dos fluxo e as variações nos aportes de calor promoveram uma sensível diminuição na quantidade de microfase para faixa de 2,5 a 10%. Entre os cordões ensaiados para avaliação de CTOD aquele com maior teor de austenita retida apresentou um CTOD menor, mostrando a influência dessa fase sobre a tenacidade. Também o tratamento térmico de alívio de tensões contribuiu para a diminuição da quantidade de microfase para a faixa de 0 a 1,5%, sendo que a microfase restante apresentou uma forma esferoidal.
Title in English
not available
Keywords in English
Iron powder addition
Submerged arc welding
Abstract in English
Previous studies showed that the welding of steel USI-SAC-50 with addition of metal powder can promote the appearing of one phase that interfere in the mechanical properties. This work had the objective of studying the effects of variations in the consumable ones, contribution of heat input and of the thermal treatment in the decrease or elimination of this phase. Plates of steel USI-SAC-50 were welded by submerged are weld with addition of metal powder being used welding fluxes BX-200 and OK-1071, welding wires EM-12K and EB-2 and heat inputs of 4,8 kJ/mm and 3,6 kJ/mm. Tension and current were maintained in 34 V and 600 A, respectively. After the welding, half of the plates was submitted to a thermal treatment of relief of tensions to 580ºC for 1 h. Mechanical tests of hardness, traction to -10ºC and CTOD to -10ºC were carried out, as well as black and white and colored metalographies were carried out for identification and quantification of phases. The chemical compositions obtained in the weld beads they were appropriate so that the amount of acicular ferrite present assured the good mechanical properties. The changes in the chemical composition, in relation to previous works, caused by the variation of the fluxes and the variations in the heat inputs they promoted a sensitive decrease in the amount of microphase for strip from 2,5 to 10%. The thermal treatment of relief of tensions also contributed to the decrease of the amount of microphase for the strip from 0 to 1,5%, and the remaining microphase presented a spherical shape.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2016-09-15
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2019. All rights reserved.