Thèse de Doctorat
DOI
10.11606/T.88.2016.tde-15092016-122338
Document
Auteur
Nom complet
Gil Eduardo Guimarães
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 1999
Directeur
Jury
Gomes, Samuel Irati Novaes (Président)
Canale, Lauralice de Campos Franceschini
Ferreira, Itamar
Ishikawa, Tomaz Toshimi
Spinelli, Dirceu
Titre en portugais
Avaliação microestrutural e das propriedades mecânicas de aço ARBL de resistência ambiental soldado a arco submerso com adição de pó metálico
Mots-clés en portugais
Adição de pó metálico
Soldagem arco submerso
Resumé en portugais
Estudos anteriores mostraram que a soldagem de aço USI-SAC-50 com adição de pó metálico pode promover o aparecimento de microfases que interferem nas propriedades mecânicas. Este trabalho, teve o objetivo de estudar os efeitos de variações nos consumíveis, aporte de calor e do tratamento térmico pós-soldagem na diminuição ou eliminação das microfases. Chapas de aço USI-SAC-50 foram soldadas por arco submerso com adição de pó metálico utilizando-se fluxos de soldagem BX-200 e OK-1071,arames de soldagem EM-12K e EB-2 e aportes de calor de 4,8 kJ/mm e 3,6 kJ/mm. Tensão e corrente foram mantidas em 34 V e 600 A, respectivamente. Após a soldagem, metade das chapas foi submetida a um tratamento térmico de alívio de tensões a 580ºC por 1 h. Foram realizados ensaios mecânicos de dureza, tração a -10ºC e CTOD a -10ºC, assim como foram realizadas metalografias preto e branco e coloridas para identificação e quantificação de fases. As composições químicas obtidas nos cordões de solda foram adequadas para que a quantidade de ferrita acicular presente assegurasse as boas propriedades mecânicas. As mudanças na composição química, em relação à trabalhos anteriores, ocasionadas pela variação dos fluxo e as variações nos aportes de calor promoveram uma sensível diminuição na quantidade de microfase para faixa de 2,5 a 10%. Entre os cordões ensaiados para avaliação de CTOD aquele com maior teor de austenita retida apresentou um CTOD menor, mostrando a influência dessa fase sobre a tenacidade. Também o tratamento térmico de alívio de tensões contribuiu para a diminuição da quantidade de microfase para a faixa de 0 a 1,5%, sendo que a microfase restante apresentou uma forma esferoidal.
Titre en anglais
not available
Mots-clés en anglais
Iron powder addition
Submerged arc welding
Resumé en anglais
Previous studies showed that the welding of steel USI-SAC-50 with addition of metal powder can promote the appearing of one phase that interfere in the mechanical properties. This work had the objective of studying the effects of variations in the consumable ones, contribution of heat input and of the thermal treatment in the decrease or elimination of this phase. Plates of steel USI-SAC-50 were welded by submerged are weld with addition of metal powder being used welding fluxes BX-200 and OK-1071, welding wires EM-12K and EB-2 and heat inputs of 4,8 kJ/mm and 3,6 kJ/mm. Tension and current were maintained in 34 V and 600 A, respectively. After the welding, half of the plates was submitted to a thermal treatment of relief of tensions to 580ºC for 1 h. Mechanical tests of hardness, traction to -10ºC and CTOD to -10ºC were carried out, as well as black and white and colored metalographies were carried out for identification and quantification of phases. The chemical compositions obtained in the weld beads they were appropriate so that the amount of acicular ferrite present assured the good mechanical properties. The changes in the chemical composition, in relation to previous works, caused by the variation of the fluxes and the variations in the heat inputs they promoted a sensitive decrease in the amount of microphase for strip from 2,5 to 10%. The thermal treatment of relief of tensions also contributed to the decrease of the amount of microphase for the strip from 0 to 1,5%, and the remaining microphase presented a spherical shape.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2016-09-15
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.