Disertación de Maestría
DOI
10.11606/D.88.2016.tde-15092016-142341
Documento
Autor
Nombre completo
Luiz Paulo Cadiolli
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1998
Director
Tribunal
Crnkovic, Ovídio Richard (Presidente)
Casteletti, Luiz Carlos
Gregolin, José Ângelo Rodrigues
Título en portugués
Estudo para viabilização da cementação gasosa através da dissociação do etanol diluído com gás nitrogênio
Palabras clave en portugués
Álcool etílico
Atividade de carbono
Cementação gasosa
Coeficiente de velocidade de transporte de carbono (β)
Resumen en portugués
Devido a necessidade de redução do consumo dos derivados de petróleo, faz-se necessária a procura da substituição destes por outras fontes viáveis no processo de cementação. Este trabalho apresenta um estudo para viabilização da cementação gasosa através da dissociação do álcool etílico diluído com gás nitrogênio. Foram feitos estudos termodinâmicos, com base em análise química das amostras dos gases retiradas do forno, analisados por um infra vermelho. Com análise dos gases CO, CO2, CH4 pode-se determinar as atividades do carbono nos gases (ag) e o coeficiente de velocidade de transporte de carbono da atmosfera para a superfície metálica (β), nas temperaturas de 870ºC, 900ºC, 930ºC, sendo que as atmosferas cementantes nestas temperaturas foram diluídas com diferentes porcentagens de gás nitrogênio. Com os resultados foi possível concluir que as diluições não interferiram no potencial de carbono, mas foi a grande responsável na diminuição no tamanho das camadas cementadas.
Título en inglés
Viability study of carburizing dissociation of ethanol diluted in nitrogen
Palabras clave en inglés
Carbon activity
Carbon coefficient of transport velocity (β)
Ethyl alcohol
Gas carburizing
Resumen en inglés
Nowadays, due to the need of reduction of the consume of petroleum derivative products, the substitution of these products for others sources is really necessary. This work presents a viability study of carburizing dissociation of ethanol diluted in nitrogen study gas. Thermodynamics studies were carried out with chemical analysis of gas samples from furnace using infrared analyser. CO, CO2 and CH4 gas analysis were used to determine the gas carbon activity (ag) and the carbon coefficient of transport velocity from atmosphere to the metallic surface (β), for the temperature of 870°C, 900°C and 930°C. The carbuzing atmosphere for these temperatures were diluted with different percentages of nitrogen gas. With carbon potential, but it was the mean responsible for the size reduction of case carburized.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2016-09-15
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.